| 牌号简介 About |
|---|
| TIPELIN® FS 471-02是一种薄膜级高密度聚乙烯共聚物（以己烯-1为共聚单体）级。该产品具有较高的分子量、很好的撕裂强度和抗DART耐滴性、低凝胶含量、良好的汽阻性能。该等级含有抗氧化剂和酸清除剂。推荐应用TIPELIN® FS 471-02用于超薄包装膜、袋子、购物袋和垃圾袋。TIPELIN® FS 471-02适用于食品接触。产品符合食品接触法规。 TIPELIN FS 471-02 is a film grade of high density polyethylene copolymer (with hexene-1 as comonomer) grade. The product has high molecular mass, very good Tear strength and Dart drop resistance, low gel content, good vapour barrier properties. The grade contains antioxidant and acid scavenger. Applications TIPELIN FS 471-02 is recommended for extra thin packaging films, bags, shopping bags and garbage bags. TIPELIN FS 471-02 is suitable for food contact. The product complies with Food Contact Regulations. |
产品描述 Product Description
用途：薄膜;包装;袋子;
加工条件：吹塑薄膜
性能特点： 可回收; 低速凝固晶点; 机械强度好-撕裂; 防潮; 抗氧化; 高分子量; 己烯共聚单体; 食品接触; Renewable resources,Low speed solidification point,Food contact compliance,Moisture resistance,Inoxidizability,High molecular weight,Good tear strength,Hexene copolymers
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.946 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
190℃，2.16kg 190℃，2.16kg |
0.18 | g/10min | ISO 1133 |
|
190℃，21.6kg 190℃，21.6kg |
15 | g/10min | ISO 1133 |
|
190℃，5.0kg 190℃，5.0kg |
0.80 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
63 | ISO 868 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
µm | ||
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，25 µm，吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，屈服，25 µm，吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，25 µm，吹塑薄膜 MD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，25 µm，吹塑薄膜 TD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact |
|||
|
25 µm，吹塑薄膜 25 µ m, blow molded film |
g | ISO 7765-1/A | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
|
MD：25 µm，吹塑薄膜 MD: 25 µ m, blow molded film |
N | ISO 6383-2 | |
|
TD：25 µm，吹塑薄膜 TD: 25 µ m, blow molded film |
N | ISO 6383-2 | |
|
Spencer Impact Spencer Impact |
|||
|
吹塑薄膜，25.0 µm Blow molded film, 25.0 µ m |
MPa | ASTM D3420 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A120 | |
|
氧感应时间 Oxygen sensing time |
|||
|
200℃ 200℃ |
min | EN 728 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
丁二烯市场3月迎暖春
2016-03-08 “节后归来，丁二烯涨势汹汹，较2月初大幅走高29.03%，零星报价至8000元(吨价,下同)，极大提振了市场人士信心。纵观后市，三四月份亚洲部分丁二烯装置进入集中检修状态，供应缩紧格局将延续，外盘市场价格震荡走坚，带动国内市场上扬。此外，备货补库也将积极开展，需求缓慢回升，交投低迷状况有望改善，可以预见，丁二烯市场3月将迎来暖春。”中国石油东北销售公司朱处长等业内人士对于丁二烯市场做出这样的判断。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |