Ultramid® 8233G HS是一种热稳定的33%玻璃纤维增强PA6注射成型化合物,具有优异的强度、刚度、高温性能和尺寸稳定性。它也可以在非热稳定(超中8233G)和/或色素版本。应用Ultramid® 8233G HS通常推荐用于动力工具外壳、除草器组件、齿轮、汽车外壳和发动机罩下应用。 Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in non-heat stabilized (Ultramid 8233G) and/or pigmented versions. Applications Ultramid 8233G HS is generally recommended for applications such as power tool housings, weed trimmer components, gears, automotive housings and under hood applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.39 | g/cm³ | ASTM D792 |
密度 Density |
1.39 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.30 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
6.4 | % | ISO 62 |
饱和 saturated |
6.4 | % | ASTM D570 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
24hr 24hr |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-40℃ -40℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
落下冲击阻力 Falling impact resistance |
|||
23℃ 23℃ |
J | Internal Method | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ||
MD MD |
1/℃ | ||
MD MD |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.60 mm 0.60 mm |
UL 94 | ||
0.71 mm 0.71 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
-40℃ -40℃ |
MPa | ISO 527-2 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
80℃ 80℃ |
MPa | ISO 527-2 | |
120℃ 120℃ |
MPa | ISO 527-2 | |
150℃ 150℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,-40℃ Fracture, -40 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ASTM D638 | |
断裂,121℃ Fracture, 121 ℃ |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ISO 527-2 | |
断裂,120℃ Fracture, 120 ℃ |
MPa | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂,-40℃ Fracture, -40 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ |
% | ASTM D638 | |
断裂,121℃ Fracture, 121 ℃ |
% | ASTM D638 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂,-40℃ Fracture, -40 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
% | ISO 527-2 | |
断裂,120℃ Fracture, 120 ℃ |
% | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
23℃ 23℃ |
MPa | ISO 178 | |
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
23℃ 23℃ |
MPa | ISO 178 | |
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
乐购将与可持续包装供应商合作,推出PET“托盘到托盘”回收计划
2021-10-26 搜料网资讯: 连锁超市乐购(Tesco)和可持续包装解决方案公司Faerch合作,将原有的托盘重新做成新的食品接触托盘,用于超市的各种产品。据悉,这是行业的首创,不仅在英国,在整 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |