| 牌号简介 About |
|---|
| 聚酰胺66中等粘度，30%玻璃纤维增强，UL94V0自熄，热稳定，很好的阻燃性也在低厚度。高机械和热性能，低收缩和高尺寸稳定性，高跟踪电阻。无PBDE/PBDF材料。UL94 V0认证-所有颜色0.88 mm-NC，BK，厚度0.75 mm-UL 746B认证-CTI UL94 1级。可用：不同颜色，释放剂（W）。 Polyamide 66 medium viscosity, 30% glass fiber reinforced, UL94 V0 self extinguishing, heat stabilized, very good flame proofing also at low thickness. High mechanical and thermal properties, low shrinkage and high dimensional stability, high tracking resistance. Material PBDE/PBDF free. UL94 V0 approved - All color at 0,88 mm - NC,BK, thickness 0,75 mm - UL 746B approved - CTI UL94 class 1. Available: different colors, release agent (W). |
产品描述 Product Description
颜色：可用颜色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 热稳定性好; 尺寸稳定性好; 含脱模剂; 耐电痕; 自熄; 阻燃; 收缩性低; Good Dimensional Stability,Low contractility,Good stripping performance,Flame Characteristics,Self-extinguishing,Heat Stabilized,Electric mark,V-0
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.56 到 1.58 | g/cm³ | ASTM D792 , ISO 1183 |
|
收缩率 Shrinkage rate |
ASTM D955 | ||
|
MD：3.2 mm MD：3.2 mm |
0.30 到 0.50 | % | ASTM D955 |
|
TD：3.2 mm TD：3.2 mm |
0.45 到 0.75 | % | ASTM D955 |
|
吸水率 Water absorption rate |
ASTM D570 , ISO 62 | ||
|
23℃，24hr 23℃，24hr |
0.50 | % | ASTM D570，ISO 62 |
|
饱和，23℃ Saturation, 23 ℃ |
4.5 | % | ASTM D570，ISO 62 |
|
Granule Humidity Granule Humidity |
% | 内部方法 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 3 |
|||
|
23℃ 23℃ 3 |
kJ/m² | ASTM D256，ISO 179 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃，3.2mm 23℃，3.2mm |
J/m | ASTM D256，ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
连续使用温度 Continuous use temperature |
|||
|
-- -- 4 |
℃ | UL 746B | |
|
-- -- 5 |
℃ | UL 746B | |
|
-- -- 8 |
℃ | UL 746B | |
|
-- -- 9 |
℃ | IEC 60216 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306/B50 , ASTM D1525 10 | |
|
球压测试 Ball pressure test |
|||
|
205℃ 205℃ |
VDE 0470 | ||
|
熔融温度 Melting temperature |
℃ | ASTM D211，ISO 121 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-30~30℃ MD：-30~30℃ |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
2 mm 2 mm |
kV/mm | ASTM D149 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
解决方案 A Solution A |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.75 mm，本色，黑色 0.75 mm, natural color, black |
UL 94 | ||
|
0.90 mm，所有颜色 0.90 mm, all colors |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
1.2 mm 1.2 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
1.2 mm 1.2 mm |
℃ | IEC 60695-2-13 | |
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 , ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ASTM D638 , ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 , ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 , ISO 178 | |
|
弯曲强度 bending strength |
|||
|
-- -- |
MPa | ISO 178 | |
|
断裂 fracture |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 6x4x50 mm |
| 3 M. with imp.0,75 mm |
| 4 M. with imp. 3 mm |
| 5 E. 0,75 mm |
| 6 M. w/o imp. 3 mm |
| 7 M. w/o imp.0,75 mm |
| 8 Short Term |
| 9 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部
塑料成分添加早产风险
2016-03-28 新华社专电美国一项研究显示，常见于塑料制品中的化学成分双酚A可能导致早产。得克萨斯大学医学分部加尔维斯顿校区的研究人员采集了被送到医院准备分娩的孕妇血液样本以及她们分娩过程中的羊水样本，发现血液中双酚A水平高的孕妇比双酚A水平低的孕妇早产几率高。研究人员解释，双酚A可能导致异常炎症，增加妊娠并发症风险，如破水早、早产。 报告作者，妇产系助理教授拉姆库马尔・梅农说：“女性总能接触到双酚A，因为它被用于制造食物容器，而且经微波炉或其他途径加热后释放到食物里的量会更多。”梅农率领 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付