牌号简介 About |
---|
EBALTA GH 707/BR是一种双组分环氧树脂,在室温下固化。由于填料非常细硬,该系统具有致密的耐压结构和坚硬的耐磨表面。与铸造型砂相比,Ebarta GH 707/BR具有很好的释放性能,低粘度铸造厚度可达30 mm。应用铸造型芯盒型板夹具压顶型性能硬耐磨抗冲击性好,浇注料抗压强度好 ebalta GH 707/BR is a two components epoxy resin, which cures at room temperature. Due to very fine and hard fillers, this system gets a dense pressure resistant structure and hard wear resistant surface. Compared to foundry mould sand ebalta GH 707/BR shows a very good release properties and low tackiness casting thickness up to 30 mm. Applications Foundry patterns Core boxes Pattern plates fixtures Coping models Properties hard abrasion resistant impact resistant well castable good compressive strength |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
6.0 到 10 | kJ/m² | ISO 179 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
1.95 到 2.05 | g/cm³ | |
粘度 viscosity |
|||
25℃ 25℃ |
6.2 到 7.8 | Pa·s | |
固化时间 Curing time |
|||
20℃ 20℃ |
10 到 12 | hr | |
储存稳定性 storage stability 2 |
|||
20 ℃ 20 ℃ 2 |
35 到 45 | min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 7619 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Martens Temperature Martens Temperature |
℃ | DIN 53458 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 200 g |
【新闻资讯】查看全部
塑料制品电线槽怎么使用 等我来告诉你
2017-10-16 1、塑料制品电线槽的安装 根据实际需要,用比量法量取所需的长度,可用钢锯或木工割锯切割,并除去切口毛刺。先用电钻将线槽底部钻上小钉孔,用螺丝与墙体紧固,接口要注意整条线槽平直。要因地制宜选择各种配件。线槽固定后将电线放入槽内扎好并加面盖即可。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |