EMERGE™ PC/ABS 7100 MED高级树脂在冲击强度、耐热性和加工性之间表现出平衡。它具有良好的流动性,是薄壁应用中注射成型的理想选择。这种树脂有天然的和定制的颜色。EMERGE™ PC/ABS 7100 MED树脂符合ISO 10993(医疗器械的生物评定),适用于批准的医疗应用。主要特征:根据ISO 10993应用进行测试:医疗应用 EMERGE™ PC/ABS 7100 MED Advanced Resin exhibits a balance of properties between impact strength, heat resistance and processability. It has excellent flow and is ideal for injection molding in thin-wall applications. This resin is available in natural and custom colors. EMERGE PC/ABS 7100 MED resin is compliant with ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics: Tested under ISO 10993 Applications: Medical Applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.11 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
230℃,3.80kg 230℃,3.80kg |
4.5 | g/10min | ASTM D1238 |
260℃,5.0kg 260℃,5.0kg |
25 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃,3.2mm,注塑成型 -30 ℃, 3.2mm, injection molding |
290 | J/m | ASTM D256 |
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,3.2 mm,注塑成型 0.45 MPa, unannealed, 3.2 mm, injection molded |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm,注塑 1.8 MPa, unannealed, 3.2 mm, injection molded |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.00 mm 1.00 mm 5 |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
干燥温度 drying temperature |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级,3.20 mm R-grade, 3.20 mm |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D638 | |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ASTM D638 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 |
备注 |
---|
1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
2 一般属性:这些不能被视为规格。 |
3 2.0 in/min |
4 标准 B (120°C/h), 压 力1 (10N) |
5 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
2020年中国双酚A行业供需现状及发展前景分析
2021-01-18 搜料网资讯: 1、双酚A行业产业链分析 双酚A行业相对于其他化工产品,具有更为明显的产业链一体化的特征。一方面,双酚A在工业生产中主要通过苯酚和丙酮在酸性介质中缩合制得, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |