| 牌号简介 About |
|---|
| NANCAR® 1041是丁二烯和丙烯腈的共聚物，具有优异的耐油性。它在低温下聚合，并含有足够的抗氧化剂，以满足正常老化条件。它固化更快，提供更高的模量和拉伸强度。NANCAR® 1041易于处理。建议用于软管、辊、填料、垫圈、薄板、鞋底和其他要求高耐油性的机械产品。 NANCAR® 1041 is a copolymer of butadiene and acrylonitrile with excellent oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It cures faster and provides higher modulus and tensile strength. NANCAR® 1041 provides easy processing. It is recommended for use in hoses, rolls, packings, gaskets, sheets, shoe soles and other mechanical goods requiring high oil resistance. |
产品描述 Product Description
用途：鞋类;管道;片材;垫圈;
性能特点： 拉伸性能好; 快速固化; 耐油; 抗氧化; 共聚物; 易加工; Excellent Processability,Inoxidizability,Good Tensile Strength,Copolymer,Grease resistance,Fast Cure
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.00 | g/cm³ | |
|
门尼粘度 Mooney viscosity |
ASTM D1646 | ||
|
ML 1+4，100℃ ML 1+4，100℃ |
82 | MU | ASTM D1646 |
|
ML 1+4，100℃ ML 1+4，100℃ 2 |
100 | MU | ASTM D1646 |
|
丙烯腈含量（Bound） Acrylonitrile content (Bound) |
41.0 | % | 内部方法 |
|
Stabilizer Stabilizer |
Non-staining | ||
|
可溶性 solubility |
|||
|
in MEK in MEK |
% | ||
|
粘度 viscosity |
ASTM D1646 | ||
|
最低限度 Minimum limit |
ASTM D1646 | ||
|
Minutes to 35 points rise，t35 Minutes to 35 points rise，t35 |
min | ASTM D1646 | |
|
Minutes to 5 points rise，t5 Minutes to 5 points rise，t5 |
min | ASTM D1646 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 3 |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 4 |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 5 |
ASTM D2240 | ||
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
300% 应变 300% strain 3 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 4 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
屈服 yield 3 |
MPa | ASTM D412 | |
|
屈服 yield 4 |
MPa | ASTM D412 | |
|
屈服 yield 5 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂 fracture 3 |
% | ASTM D412 | |
|
断裂 fracture 4 |
% | ASTM D412 | |
|
断裂 fracture 5 |
% | ASTM D412 | |
|
撕裂强度 tear strength 6 , 4 |
kN/m | ASTM D624 | |
|
压缩形变 Compression deformation 5 |
|||
|
100℃，70 hr 100℃，70 hr 5 |
% | ASTM D395 | |
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
空气中拉伸强度的变化率 The rate of change in tensile strength in air 7 |
|||
|
100℃，70 hr 100℃，70 hr 7 |
% | ASTM D573 | |
|
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 7 |
|||
|
100℃，70 hr 100℃，70 hr 7 |
% | ASTM D573 | |
|
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 7 |
|||
|
邵氏 A，100℃，70 hr Shore A, 100 ℃, 70 hr 7 |
ASTM D573 | ||
|
拉伸强度的变化率 The rate of change in tensile strength 7 |
ASTM D471 | ||
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
极限伸长率的变化率 Change rate of ultimate elongation 7 |
ASTM D471 | ||
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
邵氏硬度的变化率 The rate of change in Shore hardness 7 |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在IRM 903油中 Support A, 100 ℃, 70 hr, in IRM 903 oil |
ASTM D471 | ||
|
体积变化 Volume change 7 |
ASTM D471 | ||
|
100℃，70 hr，ASTM 标准油（1号） 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热损耗 Heat loss |
% | ASTM D5688 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Uncured |
| 3 CURED @150°C for 60 mins |
| 4 CURED @150°C for 40 mins |
| 5 CURED @150°C for 20 mins |
| 6 C 模具 |
| 7 CURED@150°C × 40 MINUTES |
|
【新闻资讯】查看全部
瑞士科学家研发出一种生产塑料聚合物的新方法
2018-07-26 瑞士科学家在24日的英国《自然・通讯》杂志上报告了一种生产塑料聚合物的新方法，可以获得与传统塑料特性相似、但是更可持续的生物塑料，且过程仅需30分钟。这项研究表明，基于可再生资源的生物塑料――瓶级聚乙烯呋喃酸酯，已能够在超短时间内获得。 2018年，联合国环境署首次聚焦一次性塑料污染问题，并将今年世界环境日的主题定为“塑战速决”，这是因为我们的地球正在被塑料包围。位于加利福尼亚和夏威夷之间的巨大海洋塑料堆积区，目前正漂浮着超过7.9万吨塑料垃圾。联合国环境署称，如不加以限制 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |