牌号简介 About |
---|
Uma-PET TF的主要特点是两面均为平面的透明薄膜。该薄膜具有良好的热、机械、光学和表面性能,同时具有良好的透明度和尺寸稳定性。应用广泛应用于一般软包装。适用于金属化和其他工业应用。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
ASTM D1204 | ||
MD:150℃,0.01 mm,30 min MD:150℃,0.01 mm,30 min |
2.5 | % | |
MD:150℃,0.012 mm,30 min MD:150℃,0.012 mm,30 min |
2.5 | % | |
MD:150℃,0.015 mm,30 min MD:150℃,0.015 mm,30 min |
2.5 | % | |
MD:150℃,0.019 mm,24 hrs MD:150℃,0.019 mm,24 hrs |
2.0 | % | |
MD:150℃,0.023 mm,30 min MD:150℃,0.023 mm,30 min |
2.0 | % | |
TD:150℃,0.01 mm,30 min TD:150℃,0.01 mm,30 min |
% | ||
TD:150℃,0.012 mm,30 min TD:150℃,0.012 mm,30 min |
% | ||
TD:150℃,0.015 mm,30 min TD:150℃,0.015 mm,30 min |
% | ||
TD:150℃,0.019 mm,30 min TD:150℃,0.019 mm,30 min |
% | ||
TD:150℃,0.023 mm,30 min TD:150℃,0.023 mm,30 min |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic 1 |
|||
与自身 - 动态 With oneself - dynamic 2 |
|||
与自身 - 动态 With oneself - dynamic 3 |
|||
与自身 - 动态 With oneself - dynamic 4 |
|||
与自身 - 动态 With oneself - dynamic 5 |
|||
与自身 - 静态 With oneself - static 6 |
|||
与自身 - 静态 With oneself - static 7 |
|||
与自身 - 静态 With oneself - static 8 |
|||
与自身 - 静态 With oneself - static 9 |
|||
与自身 - 静态 With oneself - static 10 |
|||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
薄膜厚度 film thickness |
|||
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,10 µm MD, fracture, 10 µ m |
MPa | ||
MD,断裂,12 µm MD, fracture, 12 µ m |
MPa | ||
MD,断裂,15 µm MD, fracture, 15 µ m |
MPa | ||
MD,断裂,19 µm MD, fracture, 19 µ m |
MPa | ||
MD,断裂,23 µm MD, fracture, 23 µ m |
MPa | ||
TD,断裂,10 µm TD, fracture, 10 µ m |
MPa | ||
TD,断裂,12 µm TD, fracture, 12 µ m |
MPa | ||
TD,断裂,15 µm TD, fracture, 15 µ m |
MPa | ||
TD,断裂,19 µm TD, fracture, 19 µ m |
MPa | ||
TD,断裂,23 µm TD, fracture, 23 µ m |
MPa | ||
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,10 µm MD, fracture, 10 µ m |
% | ||
MD,断裂,12 µm MD, fracture, 12 µ m |
% | ||
MD,断裂,15 µm MD, fracture, 15 µ m |
% | ||
MD,断裂,19 µm MD, fracture, 19 µ m |
% | ||
MD,断裂,23 µm MD, fracture, 23 µ m |
% | ||
TD,断裂,10 µm TD, fracture, 10 µ m |
% | ||
TD,断裂,12 µm TD, fracture, 12 µ m |
% | ||
TD,断裂,15 µm TD, fracture, 15 µ m |
% | ||
TD,断裂,19 µm TD, fracture, 19 µ m |
% | ||
TD,断裂,23 µm TD, fracture, 23 µ m |
% | ||
用量 dosage |
内部方法 | ||
10.0 µm 10.0 µm |
m²/kg | ||
12.0 µm 12.0 µm |
m²/kg | ||
15.0 µm 15.0 µm |
m²/kg | ||
19.0 µm 19.0 µm |
m²/kg | ||
23.0 µm 23.0 µm |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
ASTM D1003 | ||
10 µm 10 µm |
% | ||
12 µm 12 µm |
% | ||
15 µm 15 µm |
% | ||
19 µm 19 µm |
% | ||
23 µm 23 µm |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Wetting Tension - Plain side Wetting Tension - Plain side |
ASTM D2578 | ||
10.0 µm 10.0 µm |
dyne/cm | ||
12.0 µm 12.0 µm |
dyne/cm | ||
15.0 µm 15.0 µm |
dyne/cm | ||
19.0 µm 19.0 µm |
dyne/cm | ||
23.0 µm 23.0 µm |
dyne/cm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23 µm |
3 15 µm |
4 12 µm |
5 10 µm |
6 19 µm |
【新闻资讯】查看全部
上海两家联华超市免费提供劣质塑料袋
2016-08-01 超市提供两种塑料购物袋,一种收费,一种免费,你选哪种? 3月17日,上海市质监局执法总队突击检查了超市使用塑料购物袋的质量情况。执法人员发现,两家联华超市均提供收费塑料袋和免费塑料袋,免费塑料袋因为不要钱更受欢迎。 记者从上海市质监局获悉,免费塑料袋一般为劣质塑料袋,可能污染食品,造成人体健康危害。当天,执法人员顺藤摸瓜,在枫泾镇一处民宅内扣押近500万只劣质塑料购物袋。 “三无”塑料袋会污染食品 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |