CALIBRE™ 300V-10 系列聚碳酸酯树脂具有特别优异的抗冲击性能、耐热畸变性能和光学透明度,达到了UL94 V-2 阻燃等级。CALIBRE 300V 系列产品有三种添加剂类型: CALIBRE 301V:含脱模剂。 CALIBRE 302V:含紫外线稳定剂。 CALIBRE 303V:含脱模剂和紫外线稳定剂。 政府和业界标准: CSA (加拿大标准协会) UL (美国安全检测实验室) 应用领域: 电子元器件 照明 存储介质外壳 CALIBRE™ 300V-10 Series polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. The CALIBRE 300V series products are available in 2 additive packages: CALIBRE 302V: UV stabilizer. CALIBRE 303V: Mold release and UV stabilizer. Products may be offered in colors. Please check for availability. Complies with: CSA (Canadian Standards Association) Underwriters Laboratory, Inc. (UL) Consult the regulations for complete details. Applications: Electronic components Lighting Storage media housings |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 , ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
|
10 | g/10min | ASTM D1238 |
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
MD MD |
0.50 到 0.70 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
平衡 balance |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
ASTM D638 , ISO 527-2/50 | ||
屈服 yield |
MPa | ASTM D638 , ISO 527-2/50 | |
断裂 fracture |
MPa | ASTM D638 , ISO 527-2/50 | |
拉伸应变 Tensile strain |
ASTM D638 , ISO 527-2/50 | ||
屈服 yield |
% | ASTM D638 , ISO 527-2/50 | |
断裂 fracture |
% | ASTM D638 , ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- 3 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 3 |
MPa | ISO 178 | |
屈服 yield |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
mg | ASTM D1044 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-4A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 , ISO 180 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648,ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ASTM D1525 , ISO 306/B50 | |
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149,IEC 60243-1 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm,解决方案 A 2.00 mm, solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 4 |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index 5 |
% | ISO 4589-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
|||
-- -- |
ASTM D542 | ||
-- -- |
ISO 489 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
4 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【新闻资讯】查看全部
国际橡塑展展出热点技术 助推“中国智造”
2015-11-20 被橡塑业界公认为亚洲第一、全球第二的“CHINAPLAS国际橡塑展”将于2016年举办第三十届展会。为喜迎展会迈向新里程,2016年国际橡塑展将为业界呈现更多的精彩内容,并举办一连串的庆祝活动,邀请业界参与见证,共同分享喜悦! 因应全球生产行业的发展趋势,再加上迎合定制化及绿色环保的市场需求,“CHINAPLAS国际橡塑展”将推出更多自动化、创新及环保解决方案,继续为“中国制造”走向“中国智造”的转型升级战提供助推方案。“国际橡塑展”主办单位雅式展览服务有限公司于11月19 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |