牌号简介 About |
---|
noryl se1gfn2树脂PPE+PS混合物。20%玻璃纤维增强。无溴、无氯FR系统。UL94 v1和5va列表。RTI 110/105/110。介电强度。尺寸稳定性。适用于E/E应用。Noryl Se1gFn2树脂Noryl Se1gFn2是一种20%玻璃增强、可注射成型的改性聚苯醚树脂。为提高尺寸稳定性和良好流动性而设计,该树脂还使用无氯化、无溴FR添加剂,以达到1.5 mm时的v1 ul94额定值和2.0 mm时的ul94 5va额定值。根据IEC 60695-2-13,Noryl SE1GFN2的GWIT为800C@1.00 mm。noryl se1gfn2可能是一种很好的电气或电子应用材料,需要良好的流变性能、耐热性、抗水解性、低密度和薄壁阻燃性。根据VDE/DIN472第815部分,SE1GFN2无卤。Noryl SE1GFN2树脂PPE+PS混合物。20%玻璃纤维增强。无溴、无氯FR系统。UL94 v1列表。介电强度。尺寸稳定性。适用于E/E应用。 PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 and 5VA listing. RTI 110/105/110. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.23 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.20 to 0.50 | % | 内部方法 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.060 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
96 | J/m | ASTM D256 |
23℃ 23℃ |
110 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance 4 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
2.50 mm 2.50 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
100 mm跨距 100 mm span 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
|||
屈服,100 mm跨度 Yield, 100 mm span 3 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 50% RH |
4 0.20 in/min |
5 类型 1, 0.20 in/min |
6 类型 1, 2.0 in/min |
7 0.051 in/min |
8 0.10 in/min |
9 0.079 in/min |
10 Yield |
11 Break |
12 80*10*4 sp=62mm |
13 80*10*4 |
14 120*10*4 mm |
15 80*10*4 mm |
16 标准 B (120°C/h), 载荷2 (50N) |
17 Approximate maximum |
18 钨电极 |
【新闻资讯】查看全部 ![]()
赢创与中石化协作开发 OSN 膜技术
2017-07-03 德国特种化工企业赢创工业集团与中国石化北京化工研究所(BRICI)共同签署了共建实验室的合作协议,该实验室旨在研究和开发耐有机溶媒纳滤膜技术(OSN)工艺。 凭借坚实的技术知识和完整的OSN产品组合,赢创 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |