牌号简介 About |
---|
汉华道达尔的EVA E182L是为传统的T型模挤出涂层工艺设计的。高压管工艺中的专有聚合技术表现出良好的光学透明性、粘附性和低凝胶水平。特点:高生产率、优异的光学性能、低的凝胶强度、高的粘合强度、平衡的可拉伸性和颈部在食品包装膜、牛皮纸、铝箔和BOPP薄膜中的挤出涂层 Hanwha Total's EVA E182L is designed for conventional T-die extrusion coating process. Proprietary polymerization technology in high pressure tubular process show good optical clarity, adhesion properties and low gel level. Characteristics High productivity Excellent optical properties Low gel level High adhesion strength Well-balanced drawability and neck-in Applications Extrusion coating for food packaging film, kraft paper, aluminium foil and BOPP film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
15 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
18.0 | wt% | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
12.7 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 600 | % | ASTM D638 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
熔融温度 Melting temperature |
℃ | 内部方法 |
备注 |
---|
2 压 力1 (10N) |
【新闻资讯】查看全部
陶氏化学要封闭太阳能屋顶资料生产线
2016-07-15 与投身郭台铭怀抱的夏普太阳能继续发扬光大的命运相比,即将与杜邦合体的陶氏化学太阳能却没有前者那么幸运。 据美国密歇根州当地媒体MLive报道称,陶氏化学旗下的发电宅太阳能系统2.0(Powerhouse Solar System 2.0)太阳能屋顶材料生产线7月28日关闭,最后出货日为8月10日。 这意味着曾受到美国政府数千万美元资助的陶氏化学太阳能事业将戛然而止。距离这位世界著名的化学巨头推出雄心勃勃的绿色屋顶计划,仅仅过去四年多。 与其在 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |