牌号简介 About |
---|
Solef ® 9007聚偏氟乙烯均聚物粘度低,用于膜挤出和注射成型。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.75 to 1.80 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
230℃,3.80kg 230℃,3.80kg |
16 to 26 | g/10min | ASTM D1238 |
230℃,5.0kg 230℃,5.0kg |
20 to 38 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
2.0 to 3.0 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.040 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,1 秒,2.00 mm Shore D, 1 second, 2.00 mm |
ASTM D2240 | ||
拉伸模量 Tensile modulus 2 |
|||
23℃,2 mm 23℃,2 mm 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 3 |
|||
断裂,23℃,2 mm Fracture, 23 ℃, 2 mm 3 |
MPa | ASTM D638 | |
屈服,23℃,2 mm Yield, 23 ℃, 2 mm 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂,23℃,2 mm Fracture, 23 ℃, 2 mm 3 |
% | ASTM D638 | |
屈服,23℃,2 mm Yield, 23 ℃, 2 mm 3 |
% | ASTM D638 | |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
ASTM D1894 | ||
与自身 - 静态 With oneself - static |
ASTM D1894 | ||
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-10 转轮 1000 cycles, 1000 g, CS-10 wheels |
mg | ASTM D4060 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 4 |
|||
23℃,4mm 23℃,4mm 4 |
J/m | ASTM D6110 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D4065 | |
熔融温度 Melting temperature |
℃ | ASTM D3418 | |
结晶峰温度 Crystallization peak temperature 12 |
|||
DSC DSC 12 |
℃ | ASTM D3418 | |
结晶热 Crystallization heat |
J/g | ASTM D3418 | |
融合热量 Fusion heat |
J/g | ASTM D3418 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23 ℃,1 kHz 23 ℃,1 kHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.10 mm 0.10 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
|||
3.0 mm 3.0 mm |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4, 0.039 in/min |
3 类型 4, 2.0 in/min |
4 2 m/s |
【新闻资讯】查看全部
日本宇部兴业努力于聚碳酸酯二醇的延续生产聚氨酯技术
2019-08-14 日本宇部 兴产株式会社(TYO:4208)正在开发一种新工艺技术,该工艺可以连续生产 聚氨酯 的原料聚碳酸酯二醇(PCD)。如果该公司在这里取得成功,可能将成为第一个成功的连续生产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |