牌号简介 About |
---|
特殊中等冲击聚苯乙烯级,具有很高的光泽。该等级设计用于需要优良表面光洁度的注塑成型。名称:热塑性塑料ISO 2897-PS-I、M、O88-O6-04-18应用示例:消费电子产品、办公家具、冰箱内部组件、卫生和家用电器、珠宝和化妆品盒。 Special medium impact polystyrene grade exhibiting very high gloss. This grade is designed to be used in injection moulding where is required an excellent surface finish. Designation: Thermoplastics ISO 2897-PS-I,M,O88-O6-04-18 Applications Examples of application are consumer electronics, office furnishings, internal components of refrigerators, sanitary and household wares, jewel and cosmetic boxes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 | % | ISO 294-4 |
TD TD |
0.70 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
<=0.10 | % | ISO 62 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
6.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
导热系数 Thermal conductivity coefficient |
W/m/K | DIN 52612 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | IEC 60093 | |
表面电阻 Surface resistance |
Ω.cm | IEC 60093 | |
绝缘强度 Insulation strength |
|||
|
KV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
|
50 Hz | IEC 60250 | |
耗散因数 Dissipation factor |
|||
|
50 Hz | IEC 60250 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50mm 1.50mm |
UL-94 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
印新贸易协议对我国聚乙烯出口影响无限
2015-12-01 据普氏能源资讯11月27日新加坡报道,业内消息人士27日在新加坡表示,从新加坡到印度的聚乙烯出口量预计在两国之间一项自由贸易协议在12月1日生效以后的很长时间里才能逐渐增加。 但是,由于关税变化很小以及需求一直很差,两个市场的消息人士都预计自由贸易协议最初不会对聚乙烯出口量有多大的影响。 根据新加坡国际企业,新加坡出口印度的聚乙烯目前面临他们成本加运费价的0.6%关税。 根据印度财政部11月23日的一份声明所说,这个关税将在12月1日取消。< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |