| 牌号简介 About |
|---|
| Solanyl® C1204是一种适用于注塑和压缩成型应用的端部化合物，专门开发用于获得低熔点的生物聚合物。Solanyl® C1204可在常规生产线上加工。Solanyl® C1204是目前广泛应用的可生物降解塑料和聚烯烃的竞争替代品。Solanyl® C1204是专为获得一种具有诸如共聚聚丙烯和聚乙烯等性能的生物聚合物而开发的。Solanyl® C1204可与大多数生物聚酯或淀粉塑料混合，以降低成本。Solanyl® C1204拥有自然的感觉和外观。Solanyl® C1204是可生物降解的，其生物基碳衍生材料含量大于60%，且基于大于60%的植物基原材料。 Solanyl® C1204 is an end compound suitable for injection & compression molding applications and is specially developed to obtain a biopolymer with a low melting temperature. Solanyl® C1204 can be processed on conventional lines. Solanyl® C1204 is a competitive alternative for currently used biodegradable plastics & polyolefinsfor a wide range of applications. Solanyl® C1204 is specially developed to obtain a biopolymer with properties like co-PP and PE. Solanyl® C1204 can be mixed with most biopolyesters or starch plastics to reduce costs. Solanyl® C1204 has a natural feel & look. Solanyl® C1204 is biodegradable and has a biobased carbon derived material content of >60% and is based on >60% plant based raw materials. |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 可回收; 生物可降解; Renewable resources,Biodegradable
| 技术参数 Technical Data | |||
|---|---|---|---|
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
注塑成型 injection molding |
> 100 | kJ/m² | ISO 179/1eA |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
注塑成型 injection molding |
9.0 | kJ/m² | ISO 179/1eU |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
玻璃化转变温度 Glass transition temperature |
53.0 到 57.0 | ℃ | DSC |
|
维卡软化温度 Vicat Softening Temp |
55.0 到 60.0 | ℃ | ISO 306/A |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
100 到 120 | ℃ | 内部方法 |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Water Activity Water Activity |
内部方法 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，注塑成型 Shaw's D, injection molding |
ISO 868 | ||
|
拉伸模量 Tensile modulus |
|||
|
注塑成型 injection molding |
MPa | ||
|
正割，注塑成型 Cutting, injection molding |
MPa | ||
|
拉伸强度 tensile strength |
|||
|
注塑成型 injection molding |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服，注塑成型 Yield, injection molding |
% | ||
|
断裂，注塑成型 Fracture, injection molding |
% | ||
|
弯曲模量 Bending modulus |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ISO 1183 | |
|
表观密度 Apparent density |
g/cm³ | ISO 60 | |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
g/10min | ||
|
190℃，5.0kg 190℃，5.0kg |
g/10min | ||
|
螺旋流动长度 Spiral flow length 2 |
cm | 内部方法 | |
|
收缩率 Shrinkage rate |
% | ISO 294-4 | |
|
含水量 water content |
% | 内部方法 | |
|
熔体表观粘度 Apparent viscosity of melt |
|||
|
170℃，10.0 sec^-1 170℃，10.0 sec^-1 |
Pa·s | ||
|
170℃，100 sec^-1 170℃，100 sec^-1 |
Pa·s | ||
|
170℃，1000 sec^-1 170℃，1000 sec^-1 |
Pa·s | ||
|
180℃，10.0 sec^-1 180℃，10.0 sec^-1 |
Pa·s | ||
|
180℃，100 sec^-1 180℃，100 sec^-1 |
Pa·s | ||
|
180℃，1000 sec^-1 180℃，1000 sec^-1 |
Pa·s | ||
| 备注 |
|---|
| 2、熔体温度: 180°C |
|
【新闻资讯】查看全部 
大连商品交易所16日PE行情表
2022-02-16 大连商品交易所 日行情表 查询日期： 20 22 年 02 月 16 日 本月第 8 个交易日 本年第 27 个交易日 商品 交割月份 开盘价 最高价 最低价 收盘价 前结算价 结算价 涨跌 涨跌 1 成交量 持仓量 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付