| 牌号简介 About |
|---|
| Adiprene M 3900是一种聚碳酸酯基MDI端接液体聚氨酯预聚物。这种新的预聚物具有独特的耐热老化和抗水解性能。当与1，4丁二醇固化，这一成员的ADIPRENE家族生产高质量的硫化胶，硬度为96肖氏A。该产品的特点是：撕裂强度高，耐磨性好，耐溶剂性好，在加工温度下耐水解性好，使用寿命适合机器和手工配料。 ADIPRENE M 3900 is a polycarbonate - based, MDI-terminated liquid urethane prepolymer. This new prepolymer is unique in its resistance to heat aging and hydrolysis. When cured with 1,4 Butanediol, this member of the Adiprene family produces high quality vulcanizates that are 96 Shore A in hardness. The features of ADIPRENE M 3900 include: High Tear Strength Excellent Abrasion resistance Good Solvent Resistance Good Hydrolysis Resistance Adiprene M3900 at processing temperature has a working life suitable for both machine and hand-batching procedures. |
产品描述 Product Description
性能特点： 耐磨; 机械强度好-撕裂; 耐化学性; 耐水解; 耐老化; Good heat aging resistance,Hydrolysis stability,Good tear strength,Good wear resistance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
38.7 | MPa | ASTM D412 |
|
100% 应变 100% strain |
15.3 | MPa | ASTM D412 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
260 | % | ASTM D412 |
|
撕裂强度 tear strength |
|||
|
-- -- 2 |
111 | kN/m | ASTM D624 |
|
开裂 cracking |
23 | kN/m | ASTM D470 |
|
压缩形变 Compression deformation |
|||
|
70℃，22 hr 70℃，22 hr |
% | ASTM D395B | |
|
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
储存稳定性 storage stability |
min | ||
|
后固化时间 Post curing time |
|||
|
115℃ 115℃ |
hr | ||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
固化时间 Curing time |
|||
|
115℃ 115℃ |
hr | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
ASTM D2240 | ||
|
压缩强度 compressive strength |
ASTM D695 | ||
|
5% 应变 5% strain |
MPa | ASTM D695 | |
|
10% 应变 10% strain |
MPa | ASTM D695 | |
|
15% 应变 15% strain |
MPa | ASTM D695 | |
|
20% 应变 20% strain |
MPa | ASTM D695 | |
|
25% 应变 25% strain |
MPa | ASTM D695 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具 |
|
【新闻资讯】查看全部 
我国模具消费企业达2.5万家 销售额打破1700亿元
2016-09-14 中国模具工业协会会长武兵书在近期东莞市长安镇举行的2016首届“长安杯”中国模具作品与制造技能大赛启动仪式上指出，我国模具的制造能力从改革开放初期的数十亿元增加到2015年的2100亿元，从业人员从几万人增加到百万人，其中销售额超过1700亿元，不但基本满足了我国制造业对模具数量、品种和质量的要求，而且具备了几乎所有模具品种的批量出口能力。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付