牌号简介 About |
---|
丙烯与乙烯在复合金属有机催化剂作用下共聚得到的产物。它具有长期热稳定性增强、生产、加工和开发聚丙烯制品时的热氧化降解性能、抗静电性能。用途:玩具、运动服装、家居用品、薄壁注塑成型。技术要求:TU 2211-136-05766801-2006 Product obtained by copolymerization of propylene and ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance during PP production, processing and use of PP-made articles, antistatic properties. Application: toys, sports requisites, household commodity, thin wall injection molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | |
表观密度 Apparent density |
0.48 到 0.60 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
45 到 65 | g/10min | ASTM D1238 |
灰份含量 Ash Content |
0.025 到 0.050 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
80 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp 2 |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Thermal Creep Temperature Thermal Creep Temperature 3 |
℃ | ||
热氧化恶化 Thermal oxidation deterioration |
|||
150℃ 150℃ |
day | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
|||
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 in liquid medium under force 10 H |
3 at load 0.46 H/mm² |
【新闻资讯】查看全部
塑料人必知 | 最全黄卡引见
2019-02-14 UL黄卡对于从事塑料行业人重要性不言而喻,读懂它也是我们每个塑料人的必备功课。今天搜料就带领大家了解UL黄卡。 UL黄卡起源 在19世纪90年代,一种未经测试的新型连接器在美国各 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |