牌号简介 About |
---|
50-3100设计用于最快和最连续的高传热。50-3100比其他商用类型的散热速度快几倍。最重要的突破是处理50-3100。该系统易于混合和浇注,形成尺寸稳定的传热包。典型应用包括电源、变压器、线圈、绝缘体的封装、芯片保护层、温度探针等。 50-3100 is designed for the fastest and most continuous high heat transfer. 50-3100 measures several times faster heat dissipation than other commercially available types. The most important breakthrough is the handling of 50-3100. This system can be easily mixed and poured to form a dimensionally stable heat transfer package. Typical applications include encapsulation of power supplies, transformers, coils, insulators, protective covering for chips, temperature probes, etc… |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
|||
MD MD |
0.30 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
3.0E-5 | 1/℃ | |
导热系数 Thermal conductivity coefficient |
2.2 | W/m/K | |
热变形温度 Hot deformation temperature |
120 | ℃ | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
工作温度 working temperature |
-60.0 到 205 | ℃ | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
|||
Part B Part B |
|||
密度 Density |
|||
25℃ 25℃ |
g/cm³ | ||
粘度 viscosity |
|||
25℃ 25℃ 2 |
Pa·s | ||
25℃ 25℃ 3 |
Pa·s | ||
固化时间 Curing time |
|||
66℃ 66℃ |
hr | ||
25℃ 25℃ |
hr | ||
储存稳定性 storage stability |
|||
25 ℃ 25 ℃ |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
MPa | ||
压缩强度 compressive strength |
MPa | ||
耐电强度 Electrical strength |
kV/mm | ||
相对电容率 Relative permittivity |
|||
60 Hz 60 Hz |
|||
体积电阻率 Volume resistivity |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Part B |
3 Part A |
【新闻资讯】查看全部
Advanced Sensor Technologies采用索尔维Ryton® P…
2018-04-23 全球领先的高性能聚合物供应商索尔维今天宣布,先进传感技术有限公司(Advanced Sensor Technologies Inc.)(简称ASTi)将Ryton® 聚苯硫醚(PPS)用于两种工业级传感器保护壳。上述旨在评测工业流程中的pH 值或氧化还原电位(ORP)的传感器被包裹在采用 Ryton® R-4-230BL 模塑成型的外壳内。Ryton® R-4-230BL 是一种40% 玻纤增强的先进PPS化合物,可加工性能更为优异,即使在高温下仍具备出色的刚度和很强的耐化学性。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |