Mold Max® 14NV是一种Shore 14A锡催化硅橡胶,具有低粘度、快速固化和较长的使用寿命。模具最大14 nv不需要真空脱气。配合比为100A:10B(按重量计)。工作时间为40分钟,室温下固化时间为4小时。Mold Max® 14NV将重现最佳细节,适用于各种工业和艺术相关应用,包括制作用于复制原型、家具、雕塑和建筑元素的模具。Mold Max® 14NV也可用于制作电影特效。使用Accel-T固化加速器可以缩短固化时间。Mold Max® 14NV可用于铸造各种材料,包括混凝土、蜡、石膏、低熔合金/金属和聚氨酯、环氧树脂或聚酯树脂。重要事项:您必须使用克级秤对A和B部分进行称重,才能成功使用Mold Max® 14NV。 Mold Max® 14NV is a Shore 14A tin-catalyzed silicone rubber that offers low viscosity, fast cure and long library life. Mold Max® 14 NV does not require vacuum degassing. Mix ratio is 100A:10B by weight. Working time is 40 minutes and cure time is 4 hours at room temperature. Mold Max® 14NV will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making molds for reproducing prototypes, furniture, sculpture and architectural elements. Mold Max® 14NV can also be used to create movie special effects. Cure time can be reduced with Accel-T® cure accelerator. Mold Max® 14NV can be used to cast a variety of materials including concrete, wax, gypsum, low melt alloys/metals and urethane, epoxy or polyester resins. Important; you must weigh Part A & B components using a gram scale to be successful with Mold Max® 14NV. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.892 | cm³/g | |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 | % | ASTM D2566 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
14 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
3.38 | MPa | ASTM D412 |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
ASTM D150 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
|||
工作温度 working temperature |
℃ | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
储存稳定性 storage stability |
|||
23℃ 23℃ |
min | ASTM D2471 | |
热固性混合粘度 Thermosetting mixed viscosity |
cP | ASTM D2393 | |
脱模时间 stripping time |
|||
23℃ 23℃ |
min |
备注 |
---|
2、B 模具 |
【新闻资讯】查看全部
注塑机行业中自动化控制运用日益突出
2016-04-19 随着经济与科技水平的提高,汽车、移动电话、电子电器、食品饮料包装、塑料建材等市场也迅速发展,为之配套的塑料制品加工商为了满足终端市场对高品质塑料产品的需求,注塑机行业开始选择与整厂自动化方案提供商合作。这也是自动化控制应用注塑机行业的一大表现。 从美国、日本、德国、意大利、加拿大等主要生产国来看,中国注塑机在塑料机械当中的比重不断上升,在塑料机械中占的比重最大。塑料加工业巨大的发展潜力,为注塑机产业迅猛成长提供了发展空间。 以人工控制为本,强 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |