聚苯乙烯冲击8260是一种高冲击聚苯乙烯挤出和注射应用。与标准高冲击等级相比,该等级具有更好的抗环境应力开裂性能。该产品专门设计用于生产冰箱部件:内衬、门内衬、注入部件等。该等级也适用于生产可能导致应力开裂的产品,如脂肪、油……聚苯乙烯冲击8260在低温下保持了良好的机械性能,使该等级适合于冷冻包装;它还提供了良好的印刷性能。热成型应用表,冰箱内衬,低温包装应用(冰淇淋盒和盖子),腐蚀性食品包装,亚光处理,软接触。 POLYSTYRENE IMPACT 8260 is an high impact polystyrene for extrusioin and injection applications. This grade has an improved environmental stress crack resistance in comparison with standard high impact grades. The product has been specifically designed for the production of refrigerator part: inner liners, door liners, injected parts etc. This grade is also proposed for the production of packaging intended for products likely to cause stress cracking e.g. fats, oil... POLYSTYRENE IMPACT 8260 retains good mechanical properties at low temperatures making this grade suitable for frozen packaging; it also affords good printing performance. Applications Sheet for thermoforming, fridges liners, low temperature packaging applications (ice cream boxes and lids), packaging for aggressive foodstuffs, matt finish, soft touch. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.60 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
2.8 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
0.40 到 0.70 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.10 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
介电强度 Dielectric strength |
|||
23℃ 23℃ |
kV/mm | IEC 60243-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中国石化前三季度净利润近600亿元,同比增长154.9%
2021-10-29 搜料网资讯: 10月28日,中国石化发布2021年第三季度业绩报告。按照中国企业会计准则,前三季度公司归属于母公司股东净利润人民币598.92亿元,同比增长154.9%;按照国际财务报告准则 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |