牌号简介 About |
---|
临时数据表P5510NT是分子量双峰分布的高密度聚乙烯(天然色)。它是专为非压力管道应用而设计的。它具有良好的抗应力开裂性能(ESCR)。适用于饮用水、灌溉、波纹管、电信应用和排水管道的典型应用。也建议用于制造容器。 Provisional Data Sheet P5510NT is high density Polyethylene (Natural Color) with a bimodal distribution of molecular mass. It is specifically designed for non - pressure Pipe applications. It provides good stress crack resistance properties (ESCR). Typical Applications pipes for drinking water, irrigation, corrugated, Tele-communication application and drainage pipes. It is also recommended for manufacture of containers. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.945 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,21.6kg 190℃,21.6kg |
12 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
0.45 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
8.0 | kJ/m² | ISO 179 |
23℃ 23℃ |
23 | kJ/m² | ISO 179 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | DIN 53765 | |
氧感应时间 Oxygen sensing time |
|||
210℃ 210℃ |
min | EN 728 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
拉伸强度 tensile strength |
|||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
拉伸应变 Tensile strain |
|||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
% | ISO 527-2/1BA/50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
【新闻资讯】查看全部
高端聚烯烃大蓝海:中国石化中国石油万华荣盛宝丰卫星等巨头都在布
2021-09-13 搜料网资讯: 中国聚烯烃行业结构性矛盾加剧。一方面,中低端通用料未来产能快速增长,竞争愈发激烈;另一方面,高端及差异化产品严重依赖于进口,自给率不足五成。其中,聚烯 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |