公司信息及水印
牌号简介 About |
---|
Hyflon® MFA® 1041是一种专为阻燃型局域网电缆绝缘设计的高速挤出树脂。MFA 1041除了具有优异的防火性能、物理性能和加工性能外,还具有优异的电气性能。MFA独特的化学结构为日益苛刻的电信行业提供了必要的优越性能。采用MFA 1041制造的电缆符合电信行业协会(TIA)6类标准。mfa 1041的极低衰减使其成为开发增强6类标准的逻辑选择。由MFA 1041制成的电缆符合NFPA 90A(“空调和通风系统标准”)中规定的防火性能要求。Hyflon® MFA® 1041不建议用于需要显著热应力抗裂性的厚壁应用。 Hyflon® MFA 1041 is a high extrusion speed resin specifically designed for insulation for plenum-rated LAN cables. MFA 1041 delivers superior electrical performance in addition to its excellent fire characteristics, physical properties, and processing. The unique chemical structure of MFA provides the superior properties necessary for the increasingly demanding telecommunications industry. Cables manufactured with MFA 1041 have met the Telecommunications Industry Association (TIA) Category 6 standard. The extremely low attenuation of MFA 1041 makes it a logical choice for the developing Augmented Category 6 standard. Cables made from MFA 1041 have met the fire performance requirements called out in NFPA 90a ("Standard for Air- Conditioning and Ventilating Systems"). Hyflon® MFA 1041 is not recommended for heavy wall applications where significant thermal stress crack resistance is required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.12 到 2.17 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
372℃,5.0kg 372℃,5.0kg |
22 到 28 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
无断裂 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
280 到 290 | ℃ | ASTM D3307 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1.2E-4 到 2.0E-4 | 1/℃ | ASTM D696 |
比热 specific heat |
|||
23℃ 23℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
|||
40℃ 40℃ |
W/m/K | ASTM C177 | |
融合热量 Fusion heat |
J/g | DSC | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 4 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
23 ℃,1 MHz 23 ℃,1 MHz |
ASTM D150 | ||
23 ℃,850 MHz 23 ℃,850 MHz |
ASTM D150 | ||
23 ℃,2.10 GHz 23 ℃,2.10 GHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
23℃,1 MHz 23℃,1 MHz |
ASTM D150 | ||
23℃,850 MHz 23℃,850 MHz |
ASTM D150 | ||
23℃,2.1 GHz 23℃,2.1 GHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
潜热 latent heat |
J/g | NFPA 259 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus 2 |
|||
23℃ 23℃ 2 |
MPa | ASTM D1708 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D1708 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D1708 | |
弯曲寿命 Bending life 3 |
Cycles | ASTM D2176 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,039 in/min |
3 0.3mm 膜 |
4 50Hz |
【新闻资讯】查看全部
中共中央 国务院关于加快建设全国统一大市场的意见
2022-04-11 建设全国统一大市场是构建新发展格局的基础支撑和内在要求。为从全局和战略高度加快建设全国统一大市场,现提出如下意见。 一、总体要求 (一)指导思想。以习近平新时代中国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |