牌号简介 About |
---|
以前的名称BayBlend FR2010;(PC+ABS)混合物;未增强;阻燃;注塑等级;易流动等级;VICAT/B 120温度=108°C;UL识别94 V-0(1.5 mm);热线测试(GWFI):960°C(2.0 mm);优化的加工性;良好的光稳定性。 (PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 108°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; optimized processability; good light stability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:2.0 mm MD:2.0 mm |
0.60 | % | ISO 294-4 |
TD:2.0 mm TD:2.0 mm |
0.60 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.50 | % | ISO 62 |
23℃,50% RH 23℃,50% RH |
0.20 | % | ISO 62 |
熔体质量流动速率 Melt Flow Rate |
|||
240℃,5.0kg 240℃,5.0kg |
g/10min | ISO 1133 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
TD TD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | IEC 60093 | |
表面电阻 Surface resistance |
Ω.cm | IEC 60093 | |
绝缘强度 Insulation strength |
|||
|
KV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
23℃ 23℃ |
1 MHz | IEC 60250 | |
耗散因数 Dissipation factor |
|||
23℃ 23℃ |
1 MHz | IEC 60250 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
|
UL 94 | ||
|
UL 94 | ||
|
V-0 | UL 94 | |
2.20mm 2.20mm |
UL 94 | ||
3.00mm 3.00mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1 mm 1 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
2.2 mm 2.2 mm |
℃ | IEC 60695-2-12 | |
3 mm 3 mm |
℃ | IEC 60695-2-12 | |
灼热丝相对温度 Relative temperature of heating wire |
|||
1.00mm 1.00mm |
℃ | IEC 60695-2-13 | |
1.50mm 1.50mm |
℃ | IEC 60695-2-13 | |
2.20mm 2.20mm |
℃ | IEC 60695-2-13 | |
3.00mm 3.00mm |
℃ | IEC 60695-2-13 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 模具温度: 176°F, 熔体温度: 500°F |
3 2x8 mm |
4 150x105x3 mm, 80°C MT |
【新闻资讯】查看全部
PLA和PBAT为什么能够成为可降解塑料的宠儿?
2021-10-26 搜料网资讯: 众所周知,为改变我国白色污染的环境问题,实现双碳目标,相关部门多频次、高密度连翻出台限塑禁塑文件,大力推动传统塑料替代材料、可降解塑料材料的研发、生产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |