| 牌号简介 About |
|---|
| 20-2521是一种高性能双组分聚氨酯系统。这种易于使用的聚氨酯粘度非常低，是封装或封装精密电子元件的理想选择。20-2521在整个固化周期内表现出非常低的收缩、应力和放热。该系统还以其优异的热冲击和优异的介电性能而闻名。20-2521适用于需要较宽工作温度（-55至+130°C）的灌封应用。当接触盐水、温和的酸和碱以及脂肪族碳氢化合物时，也是一个很好的选择。特点：不含MOCA或TDI低应力元件优良的介电性能，低粘度，易于处理，收缩率低，很好的抗热震性和抗振性，水解稳定性好。 20-2521 is a high performance two component urethane system. This easy to use polyurethane is very low in viscosity and ideal for potting or encapsulating delicate electronic components. 20-2521 exhibits very low shrinkage, stress, and exotherm throughout the cure cycle. This system is also well known for its outstanding thermal shock and excellent dielectric properties. 20-2521 is ideal for potting applications where a wide operating temperature (-55 to +130°C) is required. It is also a good choice when exposure to salt water, mild acids and bases, and aliphatic hydrocarbons is expected. Features: Does not contain MOCA or TDI Low stress on components Excellent dielectric properties Low viscosity Easy to handle Low shrinkage Very good thermal shock and vibration resistance Hydrolytic stability |
产品描述 Product Description
用途：电气/电子应用领域;
颜色：黑色
加工条件：灌封
性能特点： 耐水解; 低粘度; 减震; 收缩性低; Hydrolysis stability,Low Viscosity,noise reduction,Low contractility
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.71 | % | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1.6E-4 | 1/℃ | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
4.6E+13 | ohms | |
|
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
25℃ 25℃ |
5500 | cP | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
工作温度 working temperature |
-55.0 到 130 | ℃ | |
|
冷热冲击测试 Thermal Shock Test 2 |
|||
|
-65 到 130℃ -65 to 130 ℃ 2 |
|||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
颜色 colour |
|||
|
重量混合比（PBW） Weight Mix Ratio (PBW) |
|||
|
Part A Part A |
|||
|
Part B Part B |
|||
|
体积混合比（PBV） Volume Mixing Ratio (PBV) |
|||
|
Part A Part A |
|||
|
Part B Part B |
|||
|
密度 Density |
|||
|
25℃ 25℃ 3 |
g/cm³ | ||
|
25℃ 25℃ 4 |
g/cm³ | ||
|
粘度 viscosity |
|||
|
25℃ 25℃ 3 |
Pa·s | ||
|
25℃ 25℃ 4 |
Pa·s | ||
|
固化时间 Curing time |
|||
|
85℃ 85℃ |
hr | ||
|
65℃ 65℃ |
hr | ||
|
45℃ 45℃ |
hr | ||
|
25℃ 25℃ |
hr | ||
|
储存稳定性 storage stability 5 |
|||
|
25 ℃ 25 ℃ 5 |
min | ||
|
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
吸水率 Water absorption rate |
|||
|
-- -- 6 |
% | ||
|
-- -- 7 |
% | ||
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
|||
|
拉伸强度 tensile strength |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ||
|
耐电强度 Electrical strength |
kV/mm | ||
|
相对电容率 Relative permittivity |
|||
|
100 Hz 100 Hz |
|||
|
体积电阻率 Volume resistivity |
ohms·cm | ||
|
耗散因数 Dissipation factor |
|||
|
60 Hz 60 Hz |
|||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10 cycles |
| 3 Part B |
| 4 Part A |
| 5 1 lb. mass |
| 6 After 24 hours |
| 7 After 7 days |
|
【新闻资讯】查看全部
霍尼韦尔起诉MEK化学公司侵犯其专利权
2016-12-21 2016年12月20日――霍尼韦尔(纽约证券交易所代码：HON)今日宣布对MEK化学公司(下称“MEK”)提起法律诉讼，指控该公司在美国境内销售的五氟丙烷(HFC-245fa)侵犯了霍尼韦尔一项生产工艺专利权。 HFC-245fa隶属霍尼韦尔旗下英诺威®(Enovate®)品牌，是一种用于生产泡沫绝缘材料的液体发泡剂。MEK是一家总部位于美国的化学品经销商。 霍尼韦尔是全球领先的氟产品创新者，已在研发和市场方面投资数亿美元，致力于为客户提供安全、节能以及对环 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |