牌号简介 About |
---|
BA共聚物Alcudia PA-1906是一种适用于吹塑薄膜应用的共聚物,在吹塑薄膜应用中需要良好的加工性、柔韧性和良好的机械性能。丙烯酸丁酯含量为19%。它含有抗氧化添加剂。EBA Alcudia PA-1906符合大多数国家的食品接触法规。如需更多信息或证书,请联系我们的客户服务办公室。应用膜挤出拉伸罩膜建议的熔融温度范围为160至180°C。EBA共聚物具有良好的热稳定性,如果需要,可以提高加工温度。PA-1906的加工特性与低密度聚乙烯相似,推荐使用传统的聚乙烯挤出机。 BA copolymer ALCUDIA® PA-1906 is a copolymer suitable for blown film applications where good processability, flexibility and good mechanical properties are required. The butyl acrylate content is 19%. It contains antioxidant additives. EBA ALCUDIA® PA-1906 fulfils the food contact regulations in most countries. For further information or certificates, contact our Customer Service Offices. APPLICATIONS Film extrusion Stretch hood film Recommended melt temperature range is 160 to 180°C. EBA copolymers exhibit excellent thermal stability, which allows higher processing temperatures if needed. Processing characteristics of PA-1906 are similar to LDPE and conventional Polyethylene extruders are recommended. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.60 | g/10min | ISO 1133 |
丁酯丙烯酸成分 Butyl acrylate composition |
19.0 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
100 | µm | |
拉伸强度 tensile strength |
|||
MD,断裂,100 µm,吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
25.0 | MPa | |
TD,断裂,100 µm,吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,100 µm,吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
% | ||
TD,断裂,100 µm,吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
100 µm,吹塑薄膜 100 µ m, blow molded film |
g | ISO 7765-1 | |
撕裂强度 tear strength 2 |
|||
MD,100 µm MD,100 µm |
kN/m | ||
TD,100 µm TD,100 µm |
kN/m | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
备注 |
---|
2、Blown Film |
【新闻资讯】查看全部
大亚湾经开区:加快建成世界级产业基地
2022-02-22 2022年是党的二十大隆重召开、实施十四五规划承上启下的重要一年,也是大亚湾区加快建成世界级绿色石化产业基地的重要一年。大亚湾区的三大项目在今年的广东省政府工作中被提及 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |