高性能热塑性材料,30%碳纤维增强聚醚醚酮(PEEK),半结晶,注塑和挤压用颗粒,标准流程,符合FDA食品接触标准,颜色为黑色。在静态或动态系统中用于更高强度和刚度的应用。耐磨性好,摩擦系数低,热膨胀系数低。抗腐蚀环境的化学反应。 High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contact compliant, colour black. Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
88 | ISO 868 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
28000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
265 | MPa | ISO 527-2 |
断裂,125℃ Fracture, 125 ℃ |
160 | MPa | ISO 527-2 |
断裂,175℃ Fracture, 175 ℃ |
85.0 | MPa | ISO 527-2 |
断裂,275℃ Fracture, 275 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
125℃ 125℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
275℃ 275℃ |
MPa | ISO 178 | |
压缩强度 compressive strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
200℃ 200℃ |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1U | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
玻璃化转变温度 Glass transition temperature |
ISO 11357-2 | ||
-- -- |
℃ | ISO 11357-2 | |
-- -- |
℃ | ISO 11357-2 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ISO 11359-2 | ||
< 143℃ < 143℃ |
cm/cm/℃ | ISO 11359-2 | |
> 143℃ > 143℃ |
cm/cm/℃ | ISO 11359-2 | |
MD MD |
ISO 11359-2 | ||
< 143℃ < 143℃ |
cm/cm/℃ | ISO 11359-2 | |
> 143℃ > 143℃ |
cm/cm/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
相对温度指数 Relative temperature index |
|||
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D4496 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
毒性 toxicity |
NES 713 | ||
CO content CO content |
NES 713 | ||
CO2 content CO2 content |
NES 713 | ||
Total gases Total gases |
NES 713 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 Spiral flow length |
Internal Method | ||
-- -- |
cm | Internal Method | |
-- -- |
cm | Internal Method | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,100℃ Saturation, 100 ℃ |
% | ISO 62 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 模具温度: 392°F, 熔体温度: 743°F |
4 1 mm |
5 3 mm |
6 395°C nozzle, 200°C tool |
7 Onset |
8 Midpoint |
9 Average |
10 Along flow |
11 1V |
【新闻资讯】查看全部
壳牌集团:等待在华下一个一百年
2016-02-24 2016年2月15日,全球能源产业一个全新的企业诞生。在数十年来最严峻的市场条件下,壳牌集团与英国天然气集团完成合并,形成“1+1>2”的合力,构筑一家具有非凡实力的新企业。作为这一历史性转型变革的参与者,我深感荣幸。 自我们首次宣布将与英国天然气合并以来,过去的十个月紧张而忙碌。2月15日,合并后的新公司正式开始运营,这一天对我们具有重要的里程碑意义。 这也是跌宕起伏的十个月。与我们发布合并消息时相比,原油价格下降,但这丝毫没有动摇我们对这笔交易的战 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |