牌号简介 About |
---|
特性描述:抗冲击,20%玻璃纤维增强,热稳定应用:外壳,覆盖物其在热变形温度(熔点接近40°C)下优于PA 12的优点,拉伸和弯曲强度在高湿强度下显著恢复维斯塔明D系列的PA 612化合物。Y代表特殊产品,补充了维斯塔明L系列PA 12化合物的综合选择。 Characterization: impact-resistant, 20% glass fiber reinforced, heat-stabilized Applications: housings, coverings Its advantages over PA 12 exhibit in the heat deflection temperature (melting point nearly 40 °C higher) tensile and flexural strength outstanding recovery at high wet strength The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | |
收缩率 Shrinkage rate 2 |
|||
TD TD |
0.90 | % | |
MD MD |
0.70 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
2.0 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.80 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ||
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ||
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ||
熔融温度 Melting temperature 3 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ||
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A 4 |
V | ||
解决方案 A Solution A 5 |
V | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
可燃性等级 Flammability level |
|||
1.6 mm 1.6 mm |
|||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
2、specimen 127x12.7x3.2 mm processing acc. to ISO 1874-2 |
3、2nd heating |
4、50 drops Value |
5、100 drops Value |
【新闻资讯】查看全部
油价回调后上行 化工市场仍有上涨动力
2021-04-08 搜料网资讯: 市场的变化总是突如其来,3月15日和16日国际油价连续两日下挫,合计下挫近5%,然而3月17日,受美联储3月会议决定维持利率不变,暗示年内加息次数减为两次;能源资料 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |