牌号简介 About |
---|
50-2366FR是一种新型导热聚氨酯灌封料。该柔性系统设计用于在固化期间和固化后对敏感部件施加低应力。50-2366Fr聚氨酯树脂系统是为要求低温、低收缩和优良电气性能的应用而设计的。该系统是包含表面安装组件的封装应用或任何需要低应力、导热性和阻燃性的应用的良好选择。50-2366fr适用于室外使用。对于本产品的快速固化版本,考虑50-2370fr。本产品将在20分钟内无粘性。50-2366fr具有抗真菌性,通过了抗真菌试验(mil-std-810f,方法508.5)。特点:低粘度、低应力敏感元件优良的电绝缘性能优异的耐水性、低收缩抗热震性、导热阻燃性 50-2366FR is a new thermally conductive polyurethane potting compound. This flexible system is designed for low stress on sensitive components during and after cure. 50-2366FR polyurethane resin system is formulated for applications requiring low exotherm, low shrinkage, and excellent electrical properties. This system is a good choice for potting applications containing surface mount components or any application requiring low stress, thermal conductivity and flame retardancy. 50-2366FR is suitable for outdoor use. For a very fast curing version of this product consider the 50-2370FR. This product will be tack free in 20 minutes. 50-2366FR is fungus resistant and passes Fungus Resistance Testing (MIL-STD-810F, Method 508.5). Features: Low viscosity Low stress on sensitive components Excellent electrical insulation Excellent water resistance Low shrinkage Thermal shock resistance Thermally conductive Flame retardant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1.6E-4 | 1/℃ | |
导热系数 Thermal conductivity coefficient |
1.2 | W/m/K | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
6.0E+17 | ohms | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
工作温度 working temperature |
-65.0 到 135 | ℃ | |
冷热冲击测试 Thermal Shock Test |
|||
-60 到 135℃ -60 to 135 ℃ |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
|||
Part B Part B |
|||
体积混合比(PBV) Volume Mixing Ratio (PBV) |
|||
Part A Part A |
|||
Part B Part B |
|||
密度 Density |
|||
25℃ 25℃ 2 |
g/cm³ | ||
25℃ 25℃ 3 |
g/cm³ | ||
粘度 viscosity |
|||
-- -- 2 |
Pa·s | ||
-- -- 3 |
Pa·s | ||
固化时间 Curing time |
|||
100℃ 100℃ |
hr | ||
60℃ 60℃ |
hr | ||
25℃ 25℃ |
hr | ||
贮藏期限 Storage period |
month | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吸水率 Water absorption rate |
|||
-- -- 4 |
% | ||
-- -- 5 |
% | ||
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
耐电强度 Electrical strength |
kV/mm | ||
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
|||
体积电阻率 Volume resistivity |
ohms·cm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Part B |
3 Part A |
4 24 hours immersion |
5 7 days immersion |
【新闻资讯】查看全部
央行副行长谈人民币汇率:双向波动是常态,不会出现单边升值
2022-01-18 搜料网资讯: 2022年1月18日,中国人民银行副行长刘国强在国新办新闻发布会介绍2021年金融统计数据时,详解了下一阶段包括货币政策在内的重要工作。 一是保持货币信贷总量稳定增长 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |