牌号简介 About |
---|
Westlake EF608是一种高熔融指数低密度聚乙烯树脂,适用于薄型服装薄膜和其他需要良好降深的薄膜。高熔融指数使该材料成为母粒或其他浓缩物载体的良好选择。应用/用途:配制基础树脂色母粒添加剂母粒 Westlake EF608 is a high melt index LDPE resin suggested for thin guage garment films and other films requiring excellent drawdown. The high melt index makes this material a good choice in compounding applications as a carrier for masterbatch or other concentrates. Application/Uses: Compounding base resin Color concentrates Additives masterbatches |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
9.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
割线模量 Secant modulus 2 |
|||
1% 正割,TD,51 µm,吹塑薄膜 1% secant, TD, 51 µ m, blow molded film 2 |
179 | MPa | ASTM D882 |
1% 正割,MD,51 µm,吹塑薄膜 1% secant, MD, 51 µ m, blow molded film 2 |
152 | MPa | ASTM D882 |
拉伸强度 tensile strength 2 |
|||
TD,断裂,51 µm,吹塑薄膜 TD, fracture, 51 µ m, blow molded film 2 |
MPa | ASTM D882 | |
MD,断裂,51 µm,吹塑薄膜 MD, fracture, 51 µ m, blow molded film 2 |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 2 |
|||
TD,断裂,51 µm,吹塑薄膜 TD, fracture, 51 µ m, blow molded film 2 |
% | ASTM D882 | |
MD,断裂,51 µm,吹塑薄膜 MD, fracture, 51 µ m, blow molded film 2 |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
51 µm,吹塑薄膜 51 µ m, blow molded film 2 |
g | ASTM D1709 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Test run at 23°C (73°F) and 50% relative humidity |
【新闻资讯】查看全部
汽车制造商“卷”起来了,再生塑料风云渐起!
2022-02-11 塑料在整个汽车工业中得到越来越多的应用,塑料占现代汽车平均体积的50%,这意味着再生塑料的潜力很大。随着再生塑料带来的环保理念,连高大上的汽车制造商也忍不住卷了起来。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |