牌号简介 About |
---|
产品描述:API II 505是一种中级冲击改性聚苯乙烯。这种材料提高了光泽、硬度和着色能力。用途:API II 505广泛应用于家居用品、玩具、容器、弹出式显示器及各种注塑应用。符合FDA法规21 CFR 177.1640。 Product Description: API II 505 is an intermediate grade of impact modified polystyrene. This material has improved gloss, rigidity and color ability. Application: API II 505 is widely used in house wares, toys, containers, POP displays and a wide range of injection molded applications. Complies with FDA regulation 21 CFR 177.1640. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D892 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
8.0 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
69 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
85.0 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
93.9 | ℃ | ASTM D1525 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
霍尼韦尔UOP技术成功用于全球最大单车甲醇制烯烃装置
2017-02-24 霍尼韦尔今日宣布,江苏斯尔邦石化有限公司(下称“江苏斯尔邦”)采用霍尼韦尔UOP先进的 甲醇制烯烃 (MTO)工艺 并投建的生产装置已成功通过为期十天的运行测试,确保顺利上线。当全套装置投入运营时,年产量可达83.3万吨,是目前全球最大的单车甲醇制烯烃装置。 江苏斯尔邦石化工厂坐落于江苏省连云港市,主要生产丙烯腈的原料丙烯,丙烯腈是制造服装和面料,以及用于汽车零件、安全帽和其他硬质塑料制品的高性能聚合物的主要原料。另外,该生产装置还将生产乙烯-醋酸乙烯酯共聚物(EVA)的原 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |