牌号简介 About |
---|
Vipel® K095-AAA-00是一种溶于苯乙烯的阻燃环氧酚醛乙烯基酯树脂。Vipel® K095-AAA-00是理想地适用于手工铺层,喷涂,和纤维缠绕工艺,其中突出的机械性能和耐溶剂,氧化环境,化学品和良好的热机械性能是必需的。有利于腐蚀。环氧树脂-酚醛树脂基主干化学提供了对有机溶剂的抵抗力和对酸和碱的良好抵抗力。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀信息或关于树脂是否适合任何特定化学环境的问题。阻燃性Vipel® K095-AAA-00符合ASTM E 84 I级阻燃和发烟要求。耐热性Vipel® K095-AAA-00具有优良的热机械性能。可加工性Vipel® K095-AAA-00适用于长丝缠绕和手糊工艺。 The Vipel K095-AAA-00 is a fire retardant epoxy novolac vinyl ester resin dissolved in styrene. Vipel K095-AAA-00 is ideally suited for use in hand lay-up, spray-up, and filament winding processes where outstanding mechanical properties and resistance to solvents, oxidizing environments, chemicals and good thermal mechanical properties is required. BENEFITS Corrosion The epoxy novolac-based backbone chemistry provides resistance to organic solvents and good resistance to acids and alkalies. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Fire Retardancy Vipel K095-AAA-00 meets ASTM E 84 class I requirements for flame spread and smoke development neat. Heat Temperature Resistance Vipel K095-AAA-00 has excellent thermal mechanical properties. Processability Vipel K095-AAA-00 is suitable for filament winding and hand lay up processes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
35 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
143 | ℃ | ASTM D648 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Flame Spread Index Flame Spread Index |
25.0 | ASTM E84 | |
Smoke Developed Smoke Developed |
300 | ASTM E84 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
9.0 | min | |
放热峰值 exothermic peak |
℃ | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 RVT,25℃ 25℃,Brookfield RVT |
Pa·s | ||
胶凝时间 Gelation time |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
2018充电桩开展之路在哪里 如何疾速开展
2018-01-22 工业和信息化部部长苗圩20日表示,近年来,我国充电网络建设稳步推进,公共场所、居民小区、单位内部、高速公路等主要场所覆盖率大幅提升,截至2017年底,全国共建成公共充电桩21.4万个,同比增长51%,保有量居全球首位。 苗圩说,虽然新建充电桩数量持续攀升,然而随着我国新能源汽车数量的快速增长,充电基础设施结构性供给不足问题仍日益凸显,目前我国电动汽车车桩比仅为3.5:1,整体规模仍显滞后。同时,充电设施布局仍不够合理,公共充电桩使用率还不到15%,可持续商业发展模式还没有形 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |