牌号简介 About |
---|
VITAMIDE® AI13BK8503是一种聚酰胺66(尼龙66)产品,。 它,在欧洲有供货。 特性包括: 阻燃/额定火焰 冲击改性 Chemically reinforced with 15% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. With the increasing content of FG also the toughness, tensile and bending strength increase, the shrinkage decreases and the heat application increases up to 250°C. It achieves higher rates of tensile strength and modulus of elasticity also in conditioning state when compared with PA 6 GF. PA 66 GF50 achieves modulus 16000MPa - of the aluminium alloy rates. Application: hobby tools, covers of electrotools, electromotors, cooling screws of blowers, gear wheels, carrying parts in the automotive industry like eg. brake cables. Delivered in natural mode and in the full RAL colour scale. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.23 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
275℃,0.325kg 275℃,0.325kg |
3.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
STM 64 0808 | ||
TD TD |
1.2 | % | STM 64 0808 |
MD MD |
0.80 | % | STM 64 0808 |
含水量 water content |
0.15 | % | ISO 960 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我国初次在印度洋开展微塑料污染相关迷信调查
2018-07-10 6月中下旬,西南印度洋晴空万里,海风徐徐。随着科考队员将微塑料采样器回收至“向阳红10”船甲板,中国大洋49航次第四航段科考作业顺利收官。在30多天的时间里,科考队员24小时轮班开展作业,强大的海底资源勘查设备轮番上阵,采集了大量珍贵样品和重要数据。 “目前我们的科考范围正不断向纵深发展,自主研发的海底勘查装备已经占据主导地位。中国大洋科考正以新的姿态,为国际海底区域资源开发活动和全球海洋治理贡献中国智慧!”第四航段首席科学家倪建宇信心满满。 6月15日上午 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |