CALIBRE™ 5101 聚碳酸酯树脂中添加了10%的玻璃纤维增强材料,具有更高的模量,耐热性能更好,收缩减低至最低水平。这种树脂具有优秀的UL94阻燃等级,含有脱模剂。CALIBRE 5101可提供的熔流率有8 和 15 两种。CALIBRE 5101 树脂已经根据ISO 10993 (医疗器械生物学评价)经过了生物相容性测试,适合用于获准的医疗应用领域。 主要特性: 玻璃纤维增强 阻燃 ISO 10993 应用领域 信息技术设备 电信 医疗应用领域 CALIBRE™ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL94 flammability ratings and contains mold release. CALIBRE 5101 is available in 8 and 15 melt flow rates. CALIBRE 5101 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics: Glass reinforced Ignition resistant Tested under ISO 10993 Applications Information Technology Equipment Telecommunications Medical applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.35 | % | ASTM D995 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
23℃,50% RH 23℃,50% RH |
0.25 | % | ASTM D570 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
8.0 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
|
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50mm 1.50mm |
UL-94 | ||
1.50mm 1.50mm |
UL 94 | ||
3.00mm 3.00mm |
UL 94 | ||
|
V-0 | UL 94 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
M 级 | ASTM D785 | |
洛氏硬度 Rockwell hardness |
R 级 | ASTM D785 | |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 |
备注 |
---|
1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
2 一般属性:这些不能被视为规格。 |
3 2.0 in/min |
4 方法 I (三点负荷), 0.079 in/min |
5 0.079 in/min |
6 11.1 ft/sec |
7 速率 A (50°C/h), 载荷2 (50N) |
8 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
9 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【新闻资讯】查看全部
创新甲醇制烯烃创新技术迎来新打破
2018-11-07 11月2日,上海石油化工研究院高级专家、研究七部副主任刘红星博士及科研团队正在实验室,忙于研究开发性能更优的新型S-MTO(甲醇制烯烃)催化剂。在为中原石化、中天合创及中安联合等提供MTO装置技术服务后,刘红星及科研团队并没有停止继续研发的脚步。 在我国“煤炭―合成气―甲醇―烯烃”这条产业链中,甲醇制烯烃困扰了石化产业十多年,而其他环节均已非常成熟。这就意味着只要突破甲醇制烯烃的技术瓶颈,就可走通煤制烯烃这条路,实现以煤代油。 刘红星所在团队研发的MTO技术 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |