牌号简介 About |
---|
多用途薄膜双轴取向聚丙烯(BOPP)薄膜与聚烯烃共聚物共挤出两侧。RGP是一种多用途薄膜,适用于包装各种产品,无论是单卷筒纸形式,还是层压到自身或其他基板上。rgp100和rgp120既适用于外包装,也适用于填表和密封应用。 Multi-Purpose Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with polyolefinic copolymers. RGP is a is a multi-purpose film suitable for packaging a wide range of products either in single web form, or in a lamination to itself or to other substrates. RGP100 and RGP120 are suitable for both overwrapping and form-fill-and-seal applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
内部方法 | ||
MD:129℃,1 min MD:129℃,1 min |
6.0 | % | |
TD:129℃,1 min TD:129℃,1 min |
-1.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态,外层/外层 With oneself - dynamic, outer/outer layers |
0.30 | ||
与自身 - 静态,外层/外层 Compared to itself - static, outer/outer layers |
0.30 | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
3000 | µm | |
割线模量 Secant modulus 1 |
ASTM D882 | ||
1% 正割,MD 1% secant, MD |
MPa | ||
1% 正割,TD 1% secant, TD |
MPa | ||
拉伸强度 tensile strength 2 |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ||
TD,屈服 TD, yield |
MPa | ||
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ||
TD,断裂 TD, fracture |
% | ||
密封强调 Sealing emphasis 4 |
N/mm | 内部方法 | |
始封温度 Initial sealing temperature 5 |
℃ | 内部方法 | |
透氧率 Oxygen permeability |
|||
23℃,0% RH 23℃,0% RH |
cm³·mm/m²/atm/24 hr | ASTM F1927 | |
水气透过率 Water vapor transmittance |
|||
38℃,90% RH 38℃,90% RH |
g/m²/24 hr | ASTM F1770 | |
Corona Treatment Corona Treatment |
dyne/cm | 内部方法 | |
用量 dosage |
m²/kg | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze 6 |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10%/min |
3 50%/min |
4 225°F; 1sec; 15lb/in²; untreated to untreated |
5 2secs; 15lb/in²; untreated to untreated |
6 Wide angle; 2.5° |
【新闻资讯】查看全部
美好生活,创享未来:阿科玛喜迎“绿色创新教室”五周年
2021-05-25 搜料网资讯: (2021年5月21日,中国上海)5月21日,全球领先的特种材料生产商阿科玛携员工志愿者再度来到江苏省民工子弟学校张家港市绿丰学校,续写绿色创新教室新篇章。这次活动 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |