牌号简介 About |
---|
Riblene® FL 39 D是一种低密度聚乙烯(LDPE)吹塑薄膜挤出的理想选择。Riblene® FL 39 D的特点是在可加工性、机械性能和光学性能之间有良好的平衡,由Riblene® FL 39 D制造的薄膜容易热收缩。主要应用Riblene® FL 39 D推荐用于一般吹塑薄膜应用,用于生产低规格薄膜和收缩膜,用于层压和混合。 Riblene FL 39 D is a low density polyethylene (LDPE) ideal for blown film extrusion. Riblene FL 39 D is characterised by a good balance between processability, mechanical and optical properties Films manufactured by Riblene FL 39 D are easily heat shrinkable. Main Application Riblene FL 39 D is recommended for general blown film applications, for the production of low gauge film and shrink film, for lamination and for blend. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.2 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
40 | µm | |
薄膜厚度 film thickness |
25 to 80 µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,40 µm,吹塑薄膜 1% secant, MD, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
1% 正割,TD,40 µm,吹塑薄膜 1% secant, TD, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD:40.0 µm MD:40.0 µm |
kN/m | ISO 6383-2 | |
TD:40.0 µm TD:40.0 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Blown Film |
【新闻资讯】查看全部
《财富》世界500强出炉 中企上榜数量领跑全球
2021-08-03 搜料网资讯: 8月2日,2021年《财富》世界500强排行榜发布。榜单显示,今年上榜的中国企业数量达143家,较上年增加10家,上榜企业数量再次超过美国(122家),蝉联榜首。相关人士指 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |