牌号简介 About |
---|
2235L-75透明030X是一种90C级、独特、抗萃取的柔性乙烯基化合物,具有良好的弹性、低温性能,辐照后具有优异的颜色和性能保持性。通过脂类、聚苯乙烯、聚碳酸酯或其他脂肪材料提取的组分含量极低。无邻苯二甲酸盐,2235L-75 CLEAR 030X的设计符合USP六级标准和一次性医疗器械的细胞毒性测试。 2235L-75 CLEAR 030X is a 90C rated, unique, extraction resistant flexible vinyl compound with good elasticity, low temperature performance, and excellent color and property retention after irradiation. Component extraction by lipids, polystyrene, polycarbonate or other fatty materials is extremely low. Phthalate free, 2235L-75 CLEAR 030X was designed to meet USP Class VI and cytotoxicity testing for disposable medical devices |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.21 到 1.25 | g/cm³ | ASTM D792 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 2 |
61.3 | kN/m | ASTM D1004 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
-33.0 | ℃ | ASTM D746 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,10 秒,3.18 mm Shore A, 10 seconds, 3.18 mm |
72 到 78 | ||
邵氏 A,15 秒,6.35 mm Shore A, 15 seconds, 6.35 mm |
70 到 76 | ||
拉伸模量 Tensile modulus |
|||
100% 正割,1.91 mm 100% secant, 1.91 mm |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
1.91 mm 1.91 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,1.91 mm Fracture, 1.91 mm |
% | ASTM D638 |
备注 |
---|
2. Graves |
【新闻资讯】查看全部
为克服疫情影响,大橡塑外贸打出组合拳
2020-09-22 搜料网资讯: 近日,大橡塑与国内某轮胎龙头企业欧洲子公司签订合同,为用户研制包括密炼机、挤出压片机在内的多款产品,合同额2500余万元。 受境外疫情扩散影响,国际市场需求 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |