牌号简介 About |
---|
无氯化、无溴阻燃PC/ABS,提供平衡的热量、流量和冲击,满足各种应用需求。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,2.16kg 260℃,2.16kg |
15 | g/10min | ASTM D1238 |
螺旋流动长度 Spiral flow length 2 , 3 |
68.6 | cm | Internal Method |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.40 to 0.60 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
0.40 to 0.60 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 4 |
|||
屈服 yield 4 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 4 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
|||
100 mm跨距 100 mm span 5 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
|||
屈服,100 mm跨度 Yield, 100 mm span 5 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-30℃,Energy at Peak Load -30℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
IEC 60243-1 | ||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | IEC 60243-1 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance 6 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.71 mm 0.71 mm |
UL 94 | ||
1.20 mm 1.20 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
2.00 mm 2.00 mm |
UL 94 | ||
3.40 mm 3.40 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 熔体温度: 500°F |
3 10 ips, 3.175 x 1524 mm |
4 类型 1, 2.0 in/min |
5 0.10 in/min |
6 钨电极 |
【新闻资讯】查看全部 ![]()
上半年中国四大家电产量公布,冰箱产量同比下降6.2%
2022-07-28 据国家统计局统计,2022年6月,中国空调产量2221.4万台,同比增长4.4%;1-6月,累计产量12248.9万台,同比增长1.1%。 6月,全国冰箱产量734.4万台,同比下降0.8%;1-6月,累计产量4164.2万台, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |