| 牌号简介 About |
|---|
| Ultramid® B3EG3是一种15%玻璃纤维增强注塑成型PA6级外壳具有增强的抗冲击性。典型应用包括汽车后视镜外壳和山地自行车车轮。 Ultramid B3EG3 is a 15% glass fiber reinforced injection molding PA6 grade for housings with enhanced impact resistance. Applications Typical applications include automotive mirror housings and wheels of moutain bikes. |
产品描述 Product Description
用途：汽车领域的应用;外壳;车轮;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 耐油; 冲击性能好; High impact resistance,Grease resistance,HB
填料：玻璃纤维 15
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.23 | g/cm³ | ASTM D792 |
|
密度 Density |
1.23 | g/cm³ | ISO 1183 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
275℃，5 kg 275℃，5 kg |
75.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.50 | % | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
7.7 | % | ISO 62 |
|
饱和 saturated |
% | ASTM D570 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
平衡，50% RH Balance, 50% RH |
% | ASTM D570 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
-40℃ -40℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ||
|
MD MD |
1/℃ | ASTM E831 | |
|
MD MD |
1/℃ | ||
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
UL 746 | ||
|
0.8 mm 0.8 mm |
℃ | UL 746 | |
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
UL 746 | ||
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
UL 746 | ||
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
宝泰隆拟投资6620万元 黑龙江建石墨烯消费线
2017-09-12 宝泰隆近日发布公告称，公司全资子公司七台河宝泰隆石墨烯新材料有限公司(以下简称“宝泰隆石墨烯公司”)拟建设1条50吨/年石墨烯生产线，项目建设期一年，该项目预计总投资6620万元。 该项目资金来源为公司自有资金或银行贷款，项目建设地点为黑龙江省七台河市新兴区循环经济产业园区。 该项目是公司自主研发的专利技术，在原生产线基础上扩建而成，该项目建成后，宝泰隆石墨烯公司石墨烯产能为150吨/年，其中物理法石墨烯50吨/年、化学法石墨烯100吨/年。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付