Ultramid®A 205F Natural是一种用于注塑的无增强聚酰胺66。该等级具有两个主要优点:优异的填充质量和0.4 mm以下的UL 94 V2。它特别适合薄壁长零件的成型 TECHNYL® A 205F Natural is an unreinforced polyamide 66 for injection moulding. This grade offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particularly suitable for the moulding of long parts with thin wall sections |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
成型收缩率 Mold Shrinkage Mold Shrinkage |
|||
平行 parallel Parallel |
1.7 | % | ISO 294-4 |
法向 normal Normal |
1.7 | % | ISO 294-4 |
吸水率 Water Absorption Water Absorption |
|||
24 h,23℃ 24 h,23℃ |
1.3 | % | ISO 62 |
吸湿性 Moisture Absorption Moisture Absorption |
|||
平衡,23℃。50%r.h. Equilibrium, 23 ℃. 50% r. h |
3.0 | % | ISO 62 |
密度 Density Density |
1.140 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
干燥 dry Dry |
MPa | ISO 527 | |
湿润 cond. Wet Cond |
MPa | ISO 527 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
50 mm/min,干燥 dry 50 mm/min, dry |
MPa | ISO 527-2 | |
50 mm/min,湿润 cond. 50 mm/min, moist cond |
MPa | ISO 527-2 | |
屈服 yld,2 in/min,干燥 dry Yield yld, 2 in/min, dry dry |
MPa | ASTM D638 | |
断裂 brk,干燥 dry Broken BRK, dry dry |
MPa | ISO 527-2 | |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
50 mm/min,干燥 dry 50 mm/min, dry |
% | ISO 527 | |
50 mm/min,湿润 cond. 50 mm/min, moist cond |
% | ISO 527 | |
断裂 brk,干燥 dry Broken BRK, dry dry |
% | ISO 527 | |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
% | ISO 527 | |
断裂伸长率 Elongation at Break Elongation at Break |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
干燥 dry Dry |
MPa | ISO 178 | |
湿润 cond. Wet Cond |
MPa | ISO 178 | |
干燥 dry Dry |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
干燥 dry Dry |
MPa | ISO 178 | |
湿润 cond. Wet Cond |
MPa | ISO 178 | |
干燥 dry Dry |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
干燥 dry Dry |
kJ/m² | ISO 179/1eA | |
湿润 cond. Wet Cond |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
干燥 dry Dry |
KJ/m² | ISO 180/1A | |
湿润 cond. Wet Cond |
KJ/m² | ISO 180/1A | |
干燥 dry Dry |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
1.80 MPa 1.80 MPa |
℃ | ISO 75-1/-2 | |
1.8 MPa 1.8 MPa |
℃ | ASTM D648 | |
0.45 MPa 0.45 MPa |
℃ | ASTM D648 | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
|||
干燥 dry Dry |
ohm | IEC 62631-3-2 | |
湿润 cond. Wet Cond |
ohm | IEC 62631-3-2 | |
体积电阻率 Volume Resistivity Volume Resistance |
|||
干燥 dry Dry |
ohm·m | IEC 62631-3-1 | |
湿润 cond. Wet Cond |
ohm·m | IEC 62631-3-1 | |
耐电强度 Electric strength Electric strength |
|||
d=0.8 mm d=0.8 mm |
kV/mm | IEC 60243-1 | |
d=2.0 mm d=2.0 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
1 MHz 1 MHz |
IEC 62631-2-1 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
1 MHz 1 MHz |
E-4 | IEC 62631-2-1 | |
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
|||
测试液A,干燥 dry Test solution A, dry dry |
IEC 60112 | ||
测试液A,湿润 cond. Test solution A, moisten cond |
IEC 60112 | ||
测试液B,干燥 dry Test solution B, dry dry |
IEC 60112 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
1.6 mm 1.6 mm |
calss | IEC 60695-11-10 | |
0.4 mm 0.4 mm |
calss | IEC 60695-11-10 | |
0.8 mm 0.8 mm |
calss | UL-94, IEC 60695 | |
3.2 mm 3.2 mm |
calss | UL-94, IEC 60695 | |
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) Glow Wire Flammability Index (GWFI) |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Oxygen Index Oxygen Index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
工业和信息化部:2021年原材料制造业利润同比增长92%
2022-01-20 搜料网资讯: 1月20日,国务院新闻办公室举行新闻发布会,介绍2021年工业和信息化发展情况。 工业和信息化部总工程师、新闻发言人田玉龙表示,2021年作为非常特殊的一年,努力克服 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |