Lumicene MPE M 3410 EP是以己烯为共聚单体的第二代茂金属基中密度聚乙烯。与传统的LLDPE和第一代茂金属聚乙烯相比,鲁米新MPE M 3410 EP的挤出压力低、气泡稳定性好、表观控制能力强,产量高。这些特征的结合带来了显著的下调潜力。Lumicene MPE M 3410 EP特别适用于需要高光泽和高透明度的薄膜应用,特别是在混合和与LLDPE或LDPE共挤时。Lumicene MPE M 3410 EP适用于消费者、工业、食品或卫生包装领域的许多应用,如整理收缩、邮寄膜、重型袋、袋、层压和卫生膜。 Lumicene® mPE M 3410 EP is a second generation metallocene based Medium Density Polyethylene with hexene as comonomer. Lumicene® mPE M 3410 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential. Lumicene® mPE M 3410 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE. Lumicene® mPE M 3410 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, mailing film, heavy-duty sacks, bags, lamination and hygiene film. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.934 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
40 | µm | |
拉伸强度 tensile strength |
|||
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
17.0 | MPa | |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
18.0 | MPa | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
N | ||
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
N | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blown Film Melt Temperature Blown Film Melt Temperature |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
浙江试点工程师职称制度革新 首个试点选在塑料机械行业
2017-02-24 评高工职称,不再只看论文和科研,为企业设计的产品、制定的标准反而更重要。这是最近举行的全省塑料机械高级工程师职称评审会议上实施的人才评价“新政”。 据省人力社保厅和省经信委介绍,原来评职称,专业都比较大, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-TOTAL Polyethylene Lumicene® M 3410 EP (EU - Blown Film)证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)