| 牌号简介 About |
|---|
| Lupolen 3026 K是一种加性低密度聚乙烯，具有高刚性。它含有防滑剂和防堵剂。以颗粒形式交付。有关本产品的食品法合规信息可在单独的产品文档中找到。本产品不适用于医疗和制药应用。 Lupolen 3026 K is an additivated, low density polyethylene with high rigidity. It contains slip and anti-blocking agent. It is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
产品描述 Product Description
用途：薄膜;流延薄膜;食品包装;层压板;保护涂料;
加工条件：流延薄膜
性能特点： 抗结块性; 机械强度好; 高光滑性; 低摩擦系数; 光学性能; 易加工; Good Rigidity,Excellent Processability,Smoothness,Optical performance,Low coefficient of friction,High anti-blocking
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.928 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
4.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
300 | MPa | ISO 527-2 |
|
摩擦系数 friction coefficient |
|||
|
吹塑薄膜 Blown film |
< 0.20 | ISO 8295 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
薄膜厚度 film thickness |
|||
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
屈服 yield |
MPa | ISO 527-2 | |
|
MD，50 µm，吹塑薄膜 MD, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，50 µm，吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
ASTM D2457 | ||
|
20°，50 µm，吹塑薄膜 20 °, 50 µ m, blow molded film |
ASTM D2457 | ||
|
60°，50.0 µm，吹塑薄膜 60 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Erucamide Erucamide |
% | DIN 51454 | |
|
破坏能量 Destruction energy |
|||
|
50.0 µm 50.0 µm |
J/cm | DIN 53373 | |
|
Natural Silica Natural Silica |
% | ISO 3451-1 | |
|
熔体温度 Melt Temperature |
|||
|
Film Film |
℃ | ||
| 备注 |
|---|
| 1 DIN 51454 |
| 2 Natural Silica |
| 3 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
科思创与Polymaker开以回收塑料为主的聚碳酸酯线材
2021-05-27 搜料网资讯： 日前，领先的3D打印材料制造商Polymaker使用科思创回收聚碳酸酯开发了一款名为Polymaker PC-r的聚碳酸酯线材。其原材料来自含有高纯度聚碳酸酯的农夫山泉19升水桶。科思创 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付