牌号简介 About |
---|
AdipreneL 367是一种基于聚醚的液态聚氨酯聚合物,它可以通过传统的手工和机械混合技术进行加工。当使用4,4’-亚甲基双(2-氯苯胺)或Caytur 21da氨基甲酸酯固化剂固化时,Adiprene L 367可生产46-50硬度范围内的高质量弹性体。这些坚韧、高弹性的弹性体具有许多独特的特点:优异的低温弹性、优异的耐磨性、良好的水解稳定性、良好的压缩永久性。这些特性表明,在车轮、小辊或喷涂等应用中使用了阿迪普林L 367。 ADIPRENE L 367 is a polyether-based liquid urethane polymer which is readily processable by conventional hand and machine mixing techniques. ADIPRENE L 367 produces high quality elastomers in the 46-50 durometer D hardness range when cured with 4,4'-methylene-bis (2-chloroaniline) or CAYTUR® 21DA urethane curative. These tough, highly resilient elastomers have many unique features: Excellent low-temperature flexibility Excellent abrasion resistance Good hydrolytic stability Good compression set resistance These properties suggest the use of ADIPRENE L 367 in applications such as wheels, small rolls, or spraying. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
48 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
12.4 | MPa | ASTM D412 |
300% 应变 300% strain |
30.3 | MPa | ASTM D412 |
拉伸强度 tensile strength |
42.1 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
卡-伯模量 Kappa's modulus |
ASTM D1043 | ||
-57℃ -57℃ |
MPa | ASTM D1043 | |
-40℃ -40℃ |
MPa | ASTM D1043 | |
-18℃ -18℃ |
MPa | ASTM D1043 | |
24℃ 24℃ |
MPa | ASTM D1043 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability |
min | ||
后固化时间 Post curing time |
|||
70℃ 70℃ |
hr | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
NBS NBS |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
100℃ 100℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中国页岩气开发慢上去 谁能先吃上
2015-12-22 从2014年下半年开始国际油价的持续下跌,令国内外石油上游利润被压缩。面对“寒冬”,国内外各大石油公司纷纷有针对性地调整策略,或减少勘探开发投资,或优化资产组合,剥离部分非核心油气资产增加现金流入。这令相当“烧钱”的非常规油气勘探开发处境尴尬,能源市场翘首企盼的“页岩气革命”几乎看不到踪影。 我国页岩气开发利用尚处于起步阶段,却遭遇全球页岩气发展的低谷期。我国页岩气能源发展现状如何?未来还有机会吗?在近日举行的2015非常规油气合作伙伴峰会上,多位专家建言,页岩气应当成为中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |