公司信息及水印
牌号简介 About |
---|
Bayflex XGT-100是一种用于反应注射成型(RIM)工艺的弹性聚氨酯系统。该体系分为两种液体组分:A组分为改性二苯基甲烷二异氰酸酯(MDI),B组分为聚醚多元醇体系。BayFLUX XGT-100系统的延长凝胶时间使设备设计者能够灵活地创建可在现有注塑机上成型的大型复杂零件。该树脂具有优良的表面质量和高抗冲击性,可用于农业设备、重型卡车、特种运输和海洋应用。与任何产品一样,在给定应用中使用Bayflex XGT-100系统必须由用户提前进行测试(包括现场测试等),以确定其适用性。 Bayflex XGT-100 is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two liquid components: Component A is a modified diphenylmethane diisocyanate (MDI), and Component B is a polyether polyol system. The extended gel time of Bayflex XGT-100 system gives equipment designers the flexibility to create large, complex parts that can be molded on existing injection machinery. The resin 's excellent surface quality and high impact resistance make it a candidate for agricultural equipment, heavy-duty trucks, specialty transportation, and marine applications. As with any product, use of the Bayflex XGT-100 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 | g/cm³ | ASTM D792 , ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.55 到 0.65 | % | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 2 |
|||
3.18 mm 3.18 mm 2 |
119 | kN/m | ASTM D624 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
210 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
ASTM D3763 | ||
-30℃,3.18 mm -30℃,3.18 mm |
2.71 | J | ASTM D3763 |
23℃,3.18 mm 23℃,3.18 mm |
J | ASTM D3763 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Sag(4 in Overhang,121℃,3.18 mm) Heat Sag(4 in Overhang,121℃,3.18 mm) 5 |
cm | ASTM D3769 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3.18 mm Shaw D, 3.18 mm |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃,3.18 mm -30℃,3.18 mm |
MPa | ASTM D790 | |
23℃,3.18 mm 23℃,3.18 mm |
MPa | ASTM D790 | |
70℃,3.18 mm 70℃,3.18 mm |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components 4 |
|||
部件 A Component A |
|||
部件 B Component B |
|||
脱模时间 stripping time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 7.33 ft/sec |
4 1.05 Index |
5 1 hr |
【新闻资讯】查看全部
多家PVC上市企业因涉嫌价格垄断被罚 市场降温作用清楚
2017-09-14 由于涉嫌PVC价格垄断,天原集团、英力特、亿利洁能等多家PVC企业披露收到发改委的罚单,被罚金额合计接近1亿元。上述公司均表示,罚款金额将对2017年度的利润水平造成一定影响。记者了解到,本次调查主要针对去年的涨价,已持续一定时间。对于后市的影响,从近日的PVC期货价格看,罚单对价格的冷却作用明显。不过,近期行业面临环保核查和秋季检修,开工率将下滑,供应有所减少。 多因素促价格暴涨 相关上市公司公告显示,发改委对涉嫌参与聚氯 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |