牌号简介 About |
---|
澳大利亚巴塞尔公司的聚丙烯级HP521J是一种具有常规分子量分布的中流量均聚物,专门为金属化膜生产而配制。HP521J是专为生产双轴定向金属化薄膜(BOPP)而设计的,用于高质量的包装和层压板。HP521J在BOPP拉幅机生产线上提供了可靠和一致的加工,使薄膜具有良好的性能平衡。 Basell Australia's Polypropylene grade HP521J is a medium flow homopolymer with a conventional molecular weight distribution and is specially formulated for metallised film production. HP521J is designed for the production of biaxially oriented metallised films (BOPP) for high quality packaging and laminates. HP521J gives reliable and consistent processing on BOPP tenter lines, providing films with a good balance of properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
3.0 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
4.0 | kJ/m² | ISO 180-1A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
82.0 | ℃ | ISO 75-2/B |
1.8 MPa,未退火 1.8 MPa, unannealed |
51.0 | ℃ | ISO 75-2/A |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中国聚氨酯工业协会第19次年会
2018-08-06 据8月1日举行的中国聚氨酯工业协会第19次年会消息,生态环境部已于7月28日启动消耗臭氧层物质(ODS)执法专项行动,聚氨酯硬泡发泡剂CFC-11(三氯氟甲烷)的违法使用将成为执法重点领域,发泡剂ODS淘汰已如箭在弦。 据介绍,此次执法专项行动将对全国重点行业企业组织全面排查,采取地方自查与部级巡查相结合的方式。生态环境部表示,对检查中发现含有ODS物质的原料,将追踪原料来源线索,锁定ODS物质非法生产企业。对涉及跨省的问题线索,将统一协调移交相关省份联合查办。对涉嫌生产、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |