牌号简介 About |
---|
NYCOA 1838是一种柔性尼龙共聚物TPE,适用于挤出加工和注塑成型。该树脂具有良好的韧性、柔韧性和高冲击强度,同时易于加工。NYCOA 1838推荐用于需要良好韧性和耐久性的应用。典型应用包括软触摸手柄、保龄球销底座、体育用品和柔性紧固件。 NYCOA 1838 is a flexible Nylon copolymer TPE suitable for both extrusion processing and injection molding. The resin offers excellent toughness, flexibility, and high impact strength combined with easy processability. NYCOA 1838 is recommended for applications that require good toughness and durability. Typical applications include soft-touch handles, bowling pin bases, sporting goods, and flexible fasteners. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD MD |
1.2 | % | ASTM D955 |
TD TD |
1.4 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
1.2 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
55.5 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 2 |
MPa | ASTM D790 | |
弯曲强度 bending strength 2 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
巴斯夫生物技术研发部门裁员约350人
2016-03-01 巴斯夫计划对其生物技术研发部门裁员350人左右,其中北美地区约140人,欧洲地区约180人。目前生物技术研发部门约有700人左右,基于公司新的重组计划,人员将减半。重组计划有望于今年年底完成。 巴斯夫董事会执行理事Harald Schwager表示:“生物技术部门的重组将促进巴斯夫研究项目的成功,我们很有信心。我们将终止极具挑战的技术项目,避免浪费时间和财力。” 巴斯夫是一家德国的化工企业,也是世界最大的化工厂之一。巴斯夫集团在欧洲、亚洲、南北美洲的41个国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |