| 牌号简介 About |
|---|
| 说明：SPB681/59是一种采用高压技术生产的低密度聚乙烯。用此产品获得的薄膜显示出优异的“拉伸”、良好的密封性和粘附在纸基上和低凝胶含量。该等级的最低生物基含量为95%，根据ASTM D6866测定。添加剂：抗阻塞剂：中滑剂：高应用：层压和通用薄膜。工艺：吹膜挤出。 Braskem PE SPB681/59 SPB681/59 is a low density polyethylene produced under high pressure technology. Films obtained with this product show excellent 'draw down', good sealability and adhesion on paper substrates and low gel content. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additives: Antiblocking agent: Medium Slip agent: High Applications: Films for lamination and general purpose. Process: Blown Film Extrusion. Braskem PE SPB681/59 SPB681/59 is a low density polyethylene produced under high pressure technology. Films obtained with this product show excellent 'draw down', good sealability and adhesion on paper substrates and low gel content. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additives: Antiblocking agent: Medium Slip agent: High Applications: Films for lamination and general purpose. Process: Blown Film Extrusion. Braskem PE SPB681/59 SPB681/59 is a low density polyethylene produced under high pressure technology. Films obtained with this product show excellent 'draw down', good sealability and adhesion on paper substrates and low gel content. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additives: Antiblocking agent: Medium Slip agent: High Applications: Films for lamination and general purpose. Process: Blown Film Extrusion. |
产品描述 Product Description
用途：通用;层压板;
加工条件：吹塑薄膜
性能特点： 可回收; 低速凝固晶点; 高光滑性; 无BPA; 粘结性好; 易剥离; Smoothness,Good dissection,Renewable resources,Low speed solidification point,Good bond,No BPA
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
3.8 | g/10min | ASTM D1238 |
|
Biobased Content Biobased Content |
95 | % | ASTM D6866 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
TD，断裂，38 µm，吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
20.0 | MPa | ASTM D882 |
|
MD，断裂，38 µm，吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
|||
|
TD，断裂，38 µm，吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
|
MD，断裂，38 µm，吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
|||
|
38 µm，吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
TD，38 µm，吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60°，38.0 µm，吹塑薄膜 60 °, 38.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
38 µm，吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
|