| 牌号简介 About |
|---|
| GI-1210是一种高撕裂强度、锡催化的RTV-2硅橡胶，设计用于铸造聚酯零件。GI-1210特别适用于深底切的模具和需要弯曲以拆卸零件的模具。GI-1210对抑制不敏感，这意味着它几乎可以在任何表面上在室温下固化。它很容易混合和脱气，并将固化只有轻微的收缩。橡胶硬化的速度可以用特殊的活化剂来加速。冷凝固化双组分硅橡胶非常适合大多数一般的模具制造和原型应用。它们非常适合铸造蜡、石膏、环氧树脂和其他塑料。GI-1210非常适用于需要高延伸率和中等硬度的应用。 GI-1210 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting polyester parts. GI-1210 is especially good for molds with deep undercuts and for molds that require flexing for part removal. GI-1210 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can beaccelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-1210 is extremely useful for those applications where superior elongation and medium durometer are required. |
产品描述 Product Description
用途：铸模/模具/工具;
性能特点： 机械强度好-撕裂; 收缩性低; Low contractility,Good tear strength
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.08 | g/cm³ | |
|
收缩率 Shrinkage rate |
|||
|
Cured Cured |
0.10 | % | |
|
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
颜色 colour |
|||
|
-- -- 3 |
Blue | ||
|
-- -- 4 |
Off White | ||
|
粘度 viscosity |
|||
|
-- -- 3 |
0.30 到 0.40 | Pa·s | |
|
-- -- 4 |
Pa·s | ||
|
固化时间 Curing time |
hr | ||
|
储存稳定性 storage stability 2 |
min | ||
|
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A 5 |
|||
|
邵氏 A Shaw's A 6 |
|||
|
拉伸强度 tensile strength |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D412 | |
|
撕裂强度 tear strength |
kN/m | ASTM D624 | |
|
Coverage（Cured） Coverage（Cured） |
cm³/g | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
使用温度 Operating temperature |
|||
|
Cured Cured |
℃ | ||
|
热固组件 Thermosetting components |
|||
|
树脂 resin |
|||
|
硬化法 Hardening method |
|||
|
贮藏期限 Storage period |
wk | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Mixed |
| 3 Activator |
| 4 Base |
| 5 1 Day |
| 6 7 Days |
|
【新闻资讯】查看全部
VDMA先声夺人 抢占伊朗塑胶商机
2015-12-23 12月初德国塑料和橡胶机械协会(VDMA)首次在伊朗德黑兰举办有关塑胶行业的技术会议以及B2B商务配对活动。 共有500多名来自伊朗各地的相关人士参加为期2天的活动，大部分参会代表来自伊朗的塑料和橡胶加工部门。此外，伊朗当地的树脂生产商、分支协会机构和媒体也应邀参加活动。 本次活动由VDMA主席Ulrich Reifenhäuser先生和德国驻伊朗大使Michael von Ungern-Sternberg共同主持，来自伊朗发展和创新组织(Iran Deve |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付