牌号简介 About |
---|
Plexiglas® V045i是一种轻冲击改性热塑性丙烯酸树脂,用于挤出应用。其特点是耐化学性和耐热性以及高熔体流动性。它是一种比有机玻璃v045更硬的树脂,允许改进制造。它在熔体流动和增加的抗破碎性之间提供了极好的平衡,同时提供了优于其他高冲击塑料的耐候性。 Plexiglas® V045i is a lightly impact modified thermoplastic acrylic resin formulated for extrusion applications. It is characterized by its chemical and heat resistance as well a high melt flow. It is a tougher resin than Plexiglas® V045 allowing improved fabrication. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
2.1 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 to 0.60 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
21 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 2 |
|||
1.8 MPa,退火 1.8 MPa, annealed 2 |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed 2 |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 3 | |
-- -- |
℃ | ASTM D1525 4 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 5 |
ASTM D542 | ||
透光率 Transmittance |
|||
3180 µm 3180 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
3180 µm 3180 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ASTM Classification ASTM Classification |
ASTM D788 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Annealing cycle: 4hrs @ 176°F |
3 速率 A (50°C/h), 压 力1 (10N) |
4 速率 A (50°C/h), 载荷2 (50N) |
5 ND @ 72°F |
【新闻资讯】查看全部
中美贸易摩擦 两国LDPE市场感受不同
2018-04-26 近期,中美贸易摩擦闹的沸沸腾腾,通过这一个月的硝烟升腾,大家也感受到对聚乙烯市场影响,那么在聚乙烯的影响中,两国都是怎样的感受呢? 说起这个,还是要从中国的“禁废令”说起,中国拒当全球垃圾场的禁令给全球带来的影响较为猛烈,国际上最不淡定的当属欧美国家,早在年初,美国就有网站发声,美国是全球最大的垃圾产生国,俄勒冈州则被誉为“美国环保的领头羊”,而目前在该州的一处回收场上,已堆满600吨待回收的垃圾。自2017年年10月以来,当地已被迫将800吨废品填埋。以前,俄勒冈州南部居 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |