| 牌号简介 About |
|---|
| 中等粘度，无增强聚醚醚酮VESTAKEEP® 2000G是中等粘度，无增强聚醚醚酮用于注塑成型。该半结晶聚合物具有优异的耐热性和耐化学性。VESTAKEEP® 2000G制造的零件是自动灭火的。VESTAKEEP® 2000G可由热塑性塑料常用的注塑机加工。我们建议在注射成型过程中，熔融温度在360°C到380°C之间。模具温度应在160°C至200°C的范围内，最好是180°C。 Medium-viscosity, unreinforced polyether ether ketone VESTAKEEP 2000G is a medium-viscosity, unreinforced polyether ether ketone for injection molding. The semi-crystalline polymer features superior thermal and chemical resistance. Parts made from VESTAKEEP 2000G are self-extinguishing. VESTAKEEP 2000G can be processed by common injection molding machines for thermoplastics. We recommend a melt temperature between 360°C and 380°C during the injection molding process. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C. |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 半结晶; 防火阻燃等级V-0; 耐化学性; 自熄; Self-extinguishing,Hypocrystalline,Solvent resistance,V-0
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.30 | g/cm³ | ISO 1183 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
380℃，5 kg 380℃，5 kg |
70.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate 2 |
ISO 294-4 | ||
|
TD：80℃，2.0 mm TD：80℃，2.0 mm |
1.1 | % | ISO 294-4 |
|
MD：80℃，2.0 mm MD：80℃，2.0 mm |
1.1 | % | ISO 294-4 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
3700 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2 | |
|
屈服 yield |
% | ISO 527-2 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃，完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
|
23℃，完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ISO 306/A | |
|
-- -- |
℃ | ISO 306/B | |
|
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：23~55℃ MD：23~55℃ |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength 4 |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
|
解决方案 A Solution A 5 |
V | IEC 60112 | |
|
解决方案 A Solution A |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.60 mm 1.60 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 determined on 2 mm sheets with film gate at rim mold temperature 180°C |
| 3 2nd heating |
| 4 K20/P50 |
| 5 100 drops value |
|
【新闻资讯】查看全部 
陶氏PacXpert软包装技术在日本签署第二个受权协议
2015-12-14 陶氏化学旗下陶氏包装与特种塑料业务部宣布，近日与Takigawa公司签订了PacXpert软包装技术在日本的第二个授权协议，后者将通过其日本和越南两个生产基地，向亚太区多个行业的客户提供包装产品。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |