牌号简介 About |
---|
LUBMER™ L4000是一种高分子量聚乙烯材料,。 LUBMER™ L4000的主要特性为:阻燃/额定火焰。 典型应用领域包括: 工程/工业配件 汽车行业 LUBMER™ L4000 LUBMER™ L4000 is a High Molecular Weight Polyethylene material. It is available in North America. Primary attribute of LUBMER™ L4000: Flame Rated. Typical applications include: Engineering/Industrial Parts Automotive LUBMER™ L4000 LUBMER is a specially polyethylene developed by Mitusi Chemicals' original polymerization technology. LUBMER has outstanding sliding properties, abrasion resistance and moldability. Especially, LUBMER is used for a wide range of applications for soundproofing parts of office automation equipments, automotive, electrical and electronic parts. In addition, LUBMER is making a significant contribution to the development of building materials, mechanical parts, etc.. attracting attention as a high-performance material that will build a future. Features: Sliding properties Food Safety Abrasion resistance Chemical resistance Electrical insulating properties Noiseless properties Applications: Electrical/office automation equipment parts Automotive parts General equipment parts, building materials, and other parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.967 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
TD:2.0 mm TD:2.0 mm |
1.5 | % | ASTM D955 |
MD:2.0 mm MD:2.0 mm |
1.8 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.010 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,2mm 23℃,2mm |
190 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23℃ 23℃ |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂,23℃ Fracture, 23 ℃ 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂,23℃ Fracture, 23 ℃ 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
23℃,3 mm,48 mm跨距 23 ℃, 3 mm, 48 mm span 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
|||
屈服,23℃,3 mm,48 mm跨度 Yield, 23 ℃, 3 mm, 48 mm span 3 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 5, 2.0 in/min |
3 0.20 in/min |
4 压 力1 (10N) |
【新闻资讯】查看全部
亚洲乙烯今年供应偏紧
2016-03-07 近日,有市场人士表示,今年亚洲乙烯供应将维持偏紧格局。亚洲乙烯裂解“检修小年”仍不足以平衡日本旭化成水岛50万吨/年裂解装置关闭造成的产能损失,受日本石化工业持续整合影响,今年日本乙烯出口量预计将较2015年水平有所降低。亚洲另一主要供应国韩国今年国内消费增加,可出口乙烯量预计也会减少。同时,新加坡壳牌裂解装置遭遇不可抗力而延长停工时间,中东乙烯出口也可能继续保持低水平。受此种种因素影响,亚洲终端用户可能将更多依赖来自欧洲的套利乙烯船货,北美乙烯产品也将增加出口机会。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |