牌号简介 About |
---|
EZ-Brush® Vac Bag Silicone是一种可刷洗的铂固化硅酮,专门用于制造高性能、可重复使用的真空袋。EZ-Brush® Vac Bag Silicone易于混合和涂抹。配合比为1a:1b(按体积计),橡胶可以用刷子或抹刀涂抹在垂直表面上而不会下垂。使用寿命为30分钟,重涂时间为1小时。橡胶能以可忽略的收缩率固化成具有很高延伸率和撕裂强度的柔软、柔韧的橡胶(Shore 20A)。新制作的袋子可以在3.5小时内从工具中取出,并立即用于聚酯或环氧树脂系统的生产中,并且能够承受高达500°F/260°C的温度。与传统的真空装袋系统相比,EZ-Brush® Vac Bag Silicone在交付生产就绪的硅胶袋时速度更快,从而产生巨大的时间和人力成本。维恩斯由于袋子可重复使用,长期材料成本大大降低。 EZ-Brush® Vac Bag Silicone is a brushable platinum cure silicone developed especially for making high performance, re-usable vacuum bags. EZ-Brush® Vac Bag Silicone is easy to mix and apply. Mix ratio is 1A:1B by volume and rubber can be applied with a brush or spatula to vertical surfaces without sagging. Pot life is 30 minutes, recoat time is 1 hour. Rubber cures with negligible shrinkage to a soft, flexible rubber (Shore 20A) with very high elongation and tear strength. Newly made bags can be removed from the tool in 3.5 hours and used immediately in production with polyester or epoxy resin systems and will withstand temperatures up to 500° F /260° C. Compared to conventional vacuum bagging systems, EZ-Brush® Vac Bag Silicone is much faster at delivering a production-ready silicone bag resulting in a tremendous time and labor savings. Since bags are re-usable, long term material costs are greatly reduced. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.928 | cm³/g | ASTM D1475 |
收缩率 Shrinkage rate |
|||
MD MD |
< 0.10 | % | ASTM D2566 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
20 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
3.79 | MPa | ASTM D412 |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
储存稳定性 storage stability |
|||
23℃ 23℃ |
min | ASTM D2471 | |
热固性混合粘度 Thermosetting mixed viscosity |
cP | ASTM D2393 | |
脱模时间 stripping time |
|||
23℃ 23℃ |
min |
备注 |
---|
2、B 模具 |
【新闻资讯】查看全部
欧盟委员会批准威立雅收购苏伊士,合并进入倒计时
2021-12-20 搜料网资讯: 12月14日,欧盟委员会正式批准威立雅收购苏伊士,这是威立雅完成此次并购项目的关键,也是打造全球生态转型标杆企业的决定性一步。至此,此次并购正式进入倒计时。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |