| 牌号简介 About |
|---|
| Ultramid® B3WG13 BK00102 是一种63%的玻璃增强、注塑、高模量尼龙设计，具有高强度和刚度的金属替代应用。它也有良好的可塑性和卓越的表面外观。 Ultramid B3WG13 BK00102 is a 63% glass reinforced, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldability and outstanding surface appearance. Potential applications are mirror brackets, fuel lids, gas-assisted steering wheel inserts, ski bindings and bike rack clamps. |
产品描述 Product Description
用途：室外应用;
颜色：半透明
加工条件：注射成型 Injection Molding
性能特点： 可回收; 嵌段共聚物; 防火阻燃等级HB; 抗氧化; 着色性好; 电气性好; 耐臭氧; 食品接触; 耐候抗UV; 易加工; Weather resistance is good,Excellent Processability,Good Electrical Properties,Renewable resources,Food contact compliance,Block Copolymer,Inoxidizability,Ozone resistance,Good coloring,HB
紫外线：UV Stabilized
填料：玻璃纤维 63
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.74 | g/cm³ | ASTM D792 |
|
密度 Density |
1.74 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.20 | % | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
22000 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
235 | MPa | ISO 527-2 |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
23℃ 23℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
UL 746 | ||
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
UL 746 | ||
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
UL 746 | ||
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 B 方法，直角形试样（不割口） |
|
【新闻资讯】查看全部 
滨化集团与大连物化所签约战略合作
2022-08-31 扫描上图二维码，可以免费下载 搜料 APP 8月29日，滨化集团股份有限公司（以下简称滨化集团）与中国科学院大连化学物理研究所（以下简称大连化物所）签署战略合作协议。 大连化物 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付